- Solvay Specialty Polymers Solef® 11010 Polyvinylidene Fluoride (PVDF) (Unverified Data**)
Solvay Specialty Polymers Solef® 11010 Polyvinylidene Fluoride (PVDF) (Unverified Data**)
| Category | Polymer , Thermoplastic , Fluoropolymer , PVDF , Polyvinylidinefluoride (PVDF), Molded/Extruded |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay Specialty Polymers Solef® 11010 Polyvinylidene Fluoride (PVDF)
(Unverified Data**).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Solef® 11010 PVDF is a medium-viscosity flexible PVDF copolymer resin and is typically processed by extrusion.Information provided by Solvay Specialty Polymers.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.75 - 1.80 g/cc | 1.75 - 1.80 g/cc | ASTM D792 |
| Water Absorption | <= 0.040 % @Temperature 23.0 °C, Time 86400 sec |
<= 0.040 % @Temperature 73.4 °F, Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.020 - 0.030 cm/cm | 0.020 - 0.030 in/in | |
| Melt Flow | 4.0 - 8.0 g/10 min @Load 5.00 kg, Temperature 230 °C |
4.0 - 8.0 g/10 min @Load 11.0 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 70 - 75 @Thickness 2.00 mm, Time 1.00 sec |
70 - 75 @Thickness 0.0787 in, Time 0.000278 hour |
ASTM D2240 |
| Tensile Strength at Break | 20.0 - 40.0 MPa @Thickness 2.00 mm, Temperature 23.0 °C |
2900 - 5800 psi @Thickness 0.0787 in, Temperature 73.4 °F |
Type IV, 50 mm/min; ASTM D638 |
| Tensile Strength, Yield | 20.0 - 35.0 MPa @Thickness 2.00 mm, Temperature 23.0 °C |
2900 - 5080 psi @Thickness 0.0787 in, Temperature 73.4 °F |
Type IV, 50 mm/min; ASTM D638 |
| Elongation at Break | 200 - 600 % @Thickness 2.00 mm, Temperature 23.0 °C |
200 - 600 % @Thickness 0.0787 in, Temperature 73.4 °F |
Type IV, 50 mm/min; ASTM D638 |
| Elongation at Yield | 10 - 12 % @Thickness 2.00 mm, Temperature 23.0 °C |
10 - 12 % @Thickness 0.0787 in, Temperature 73.4 °F |
Type IV, 50 mm/min; ASTM D638 |
| Tensile Modulus | 0.800 - 1.20 GPa @Thickness 2.00 mm, Temperature 23.0 °C |
116 - 174 ksi @Thickness 0.0787 in, Temperature 73.4 °F |
Type IV, 1.0 mm/min; ASTM D638 |
| Impact | 150 - 200 @Thickness 4.00 mm |
150 - 200 @Thickness 0.157 in |
J/m Charpy Notched Impact Strength; 2 m/s; ASTM D6110 |
| Coefficient of Friction, Dynamic | 0.15 - 0.35 | 0.15 - 0.35 | vs. Itself; ASTM D1894 |
| Coefficient of Friction, Static | 0.20 - 0.40 | 0.20 - 0.40 | vs. Itself; ASTM D1894 |
| Taber Abrasion, mg/1000 Cycles | 5.0 - 15 @Load 1.00 kg |
5.0 - 15 @Load 2.20 lb |
CS-10 Wheel; ASTM D4060 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Heat of Fusion | 30.0 - 40.0 J/g | 12.9 - 17.2 BTU/lb | Crystallization Heat; ASTM D3417 |
| 35.0 - 40.0 J/g | 15.1 - 17.2 BTU/lb | ASTM D3417 | |
| CTE, linear, Parallel to Flow | 180 µm/m-°C @Temperature 0.000 - 40.0 °C |
100 µin/in-°F @Temperature 32.0 - 104 °F |
ASTM D696 |
| Specific Heat Capacity | 1.20 J/g-°C @Temperature 23.0 °C |
0.287 BTU/lb-°F @Temperature 73.4 °F |
ASTM E968 |
| 1.60 J/g-°C @Temperature 100 °C |
0.382 BTU/lb-°F @Temperature 212 °F |
ASTM E968 | |
| Thermal Conductivity | 0.190 W/m-K @Temperature 23.0 °C |
1.32 BTU-in/hr-ft²-°F @Temperature 73.4 °F |
ASTM C177 |
| Melting Point | 158 - 162 °C | 316 - 324 °F | ASTM D3418 |
| Crystallization Temperature | 115 - 130 °C | 239 - 266 °F | Peak, DSC; ASTM D3418 |
| Vicat Softening Point | 90.0 - 105 °C | 194 - 221 °F | Rate A (50°C/h), Loading 2 (50 N); ASTM D1525 |
| Glass Transition Temp, Tg | -35.0 °C | -31.0 °F | ASTM D4065 |
| Flammability, UL94 | V-0 @Thickness 0.100 mm |
V-0 @Thickness 0.00394 in |
UL 94 |
| Oxygen Index | 44 % @Thickness 3.00 mm |
44 % @Thickness 0.118 in |
ASTM D2863 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+14 ohm-cm | >= 1.00e+14 ohm-cm | ASTM D257 |
| Surface Resistance | >= 1.00e+14 ohm | >= 1.00e+14 ohm | ASTM D257 |
| Dielectric Constant | 7.0 - 10 @Frequency 1.00e+6 Hz, Temperature 23.0 °C |
7.0 - 10 @Frequency 1.00e+6 Hz, Temperature 73.4 °F |
ASTM D150 |
| Dielectric Strength | 20.0 - 25.0 kV/mm @Thickness 1.00 mm, Temperature 23.0 °C |
508 - 635 kV/in @Thickness 0.0394 in, Temperature 73.4 °F |
ASTM D149 |
| Dissipation Factor | 0.20 @Frequency 1.00e+6 Hz, Temperature 23.0 °C |
0.20 @Frequency 1.00e+6 Hz, Temperature 73.4 °F |
ASTM D150 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| North America | ||
| South America | ||
| Features | Copolymer | |
| Good Flexibility | ||
| Medium Viscosity | ||
| Generic | PVDF | |
| Processing Method | Extrusion |
Users viewing this material also viewed the following:
- Sibur SKI-3S 1st Grade, 2nd Group Isoprene Rubber (IR)
- SABIC Innovative Plastics LNP Thermocomp GX061104 PSU (Europe-Africa-Middle East)
- Struktol TR 060 Blending Aid, Processing Additive
- Samsung Cheil Industries Starex® VH-0850 ABS, Unreinforced FR
- Zhejiang Juner PA-A6-1 MF25%
- DSM Akulon® F223-D (Dry) Low/Medium Viscosity Nylon 6 (North America)
- ChevronTexaco FM Silicone Spray Oil
- CP-Polymer-Technik Wellamid® 6000 GS 50 HWCP 50% Glass Sphere Filled Nylon 6, Heat Stabilized, Dry
- Arlon 930-10Xxx-P0 0.030" (0.762 mm) Self-Fusing Silicone Tape
- Ascend Performance Materials Vydyne® 20NSP BLK Nylon 66, Conditioned
Copyright © lookpolymers.com All Rights Reserved