Solvay Specialty Polymers Radel® R-5900 Polyphenylsulfone (PPSU)

Category Polymer , Thermoplastic , Polyphenylsulfone (PPSU)
Manufacturer Solvay Specialty Polymers
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers Radel® R-5900 Polyphenylsulfone (PPSU).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Radel® R-5900 polyphenylsulfone (PPSU) offers medium melt viscosities for long flow lengths and greater injection molding ease. It also provides exceptional hydrolytic stability and toughness that is superior to that of other commercially available, high-temperature engineering resins. It offers high deflection temperature and outstanding resistance to environmental stress cracking. The resin is inherently flame retardant and has excellent thermal stability and good electrical properties.Features: Acid Resistant; Base Resistant; Flame Retardant; Good Chemical Resistance; Good Flow; Good Thermal Stability; High ESCR (Stress Crack Resist.); High Heat Resistance; Hydrolytically Stable; Steam Sterilizable; Ultra High ToughnessUses: Appliances; Consumer Applications; Food Service ApplicationsInformation provided by Solvay Specialty Polymers.
Physical Properties Metric English Comments
Density 1.29 g/cc
0.0466 lb/in³
ASTM D792
Water Absorption 0.37 %

@Time 86400 sec
 0.37 %

@Time 24.0 hour
 ISO 62
Linear Mold Shrinkage, Flow 0.0070 cm/cm

@Thickness 3.18 mm
 0.0070 in/in

@Thickness 0.125 in
Melt Flow 26 - 36 g/10 min

@Load 5.00 kg,
Temperature 365 °C
 26 - 36 g/10 min

@Load 11.0 lb,
Temperature 689 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength 70.3 MPa

@Thickness 3.18 mm
 10200 psi

@Thickness 0.125 in
 ASTM D638
Elongation at Break 60 - 120 %

@Thickness 3.18 mm
 60 - 120 %

@Thickness 0.125 in
 ASTM D638
Elongation at Yield 7.2 %

@Thickness 3.18 mm
 7.2 %

@Thickness 0.125 in
 ASTM D638
Tensile Modulus 2.34 GPa

@Thickness 3.18 mm
 339 ksi

@Thickness 0.125 in
 ASTM D638
Flexural Strength 100 MPa

@Strain 5.00 %
 14500 psi

@Strain 5.00 %
 ASTM D790
Flexural Modulus 2.34 GPa

@Thickness 3.18 mm
 339 ksi

@Thickness 0.125 in
 ASTM D790
Izod Impact, Notched 6.90 J/cm

@Thickness 3.18 mm
 12.9 ft-lb/in

@Thickness 0.125 in
 ASTM D256
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 56.0 µm/m-°C

@Thickness 3.18 mm
 31.1 µin/in-°F

@Thickness 0.125 in
Deflection Temperature at 1.8 MPa (264 psi) 207 °C

@Thickness 3.20 mm
 405 °F

@Thickness 0.126 in
 Unannealed; ASTM D648
Glass Transition Temp, Tg 220 °C
428 °F
ASTM E1356
Flammability, UL94 V-0

@Thickness 0.750 mm
 V-0

@Thickness 0.0295 in
Compliance Properties Metric English Comments
NSF Yes
Yes
NSF 51
Processing Properties Metric English Comments
Melt Temperature 360 - 391 °C
680 - 736 °F
Mold Temperature 138 - 163 °C
280 - 325 °F
Drying Temperature 149 °C
300 °F
171 °C

@Time 14400 sec
 340 °F

@Time 4.00 hour
Descriptive Properties Value Comments
Agency Ratings NSF 51
Availability Asia Pacific
Europe
Latin America
North America
Color Amber; Clear/Transparent
Form Pellets
Processing Technique Injection Molding
RoHS Compliance RoHS Compliant
Screw Compression Ratio 2.2:1.0