- Polyram RamTal PM3007G5 Polyacetal for Injection Molding, 25% Glass Fiber Reinforced
Polyram RamTal PM3007G5 Polyacetal for Injection Molding, 25% Glass Fiber Reinforced
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, 30% Glass Fiber Reinforced |
| Manufacturer | Polyram |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polyram RamTal PM3007G5 Polyacetal for Injection Molding, 25% Glass Fiber Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
25% Glass fiber reinforced polyacetal for injection molding applications.Information provided by Polyram.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.58 g/cc | 0.0571 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.30 % | 0.30 % | 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.20 % | 0.20 % | ISO 62 |
| Linear Mold Shrinkage | 0.0040 - 0.010 cm/cm | 0.0040 - 0.010 in/in | ISO 2577 |
| Melt Flow | 8.5 g/10 min @Load 2.16 kg, Temperature 190 °C |
8.5 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 99 | 99 | |
| Tensile Strength, Yield | 110 MPa | 16000 psi | ISO 527 |
| Elongation at Break | 2.5 % | 2.5 % | ISO 527 |
| Flexural Strength | 200 MPa | 29000 psi | ISO 178 |
| Flexural Modulus | 7.00 GPa | 1020 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 8.00 kJ/m² | 3.81 ft-lb/in² | ISO 180 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 166 °C | 331 °F | ISO 11357 |
| Deflection Temperature at 0.46 MPa (66 psi) | 165 °C | 329 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 160 °C | 320 °F | ISO 75 |
| Flammability, UL94 | HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
|
| Flame Spread | 40 mm/min | 1.6 in/min | FMVSS302 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | IEC 60093 |
| Dielectric Strength | 20.0 kV/mm | 508 kV/in | IEC 60250 |
Users viewing this material also viewed the following:
- PolyOne OnFlex™ V 3085A-S0098 Thermoplastic Elastomer (TPE)
- Polimeri Europa Eraclene® ML 70 U High Density Polyethylene - Injection Molding
- Polymer Resources PC/ASA-GP2 Polycarbonate/ASA Alloy
- Total Finaprene® 602 Styrene-Butadiene TPE Copolymer Compound, Formulated to 57 Shore A (discontinued **)
- Gouda Vuurvast VIBRON 130 Dense Vibrating Refractory Castable
- Shakespeare S-3 Economy Nylon Copolymer Fishing Line, 70 lb
- EMS-Grivory Grivory® XE 4108 black 9992 PA612-GF50
- ACC MM828 Low Tear Condensation Cure 2-Part Molding Rubber
- Ametek AM 388™ Alloy (UNS C72650) TM06
- SABIC Innovative Plastics Noryl EUN1240 PPE+HIPS (Asia Pacific)
Copyright © lookpolymers.com All Rights Reserved