Solvay Specialty Polymers KetaSpire® KT-820 SL30 Polyetheretherketone (PEEK)
| Category | Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK) |
| Manufacturer | Solvay Specialty Polymers |
| Trade Name | KetaSpire® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay Specialty Polymers KetaSpire® KT-820 SL30 Polyetheretherketone (PEEK).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
KetaSpire® KT-820 SL30 is a polyetheretherketone (PEEK) compound designed to provide a balance of excellent mechanical properties, wear resistance and low coefficient of friction in both dry and externally lubricated applications. The resin is formulated with a ternary anti-friction/anti-wear additive system comprised of carbon fiber, graphite, and polytetrafluoroethylene (PTFE).
KetaSpire® PEEK is produced to the highest industry standards and is characterized by a distinct combination of properties, which include excellent wear resistance, best-in-class fatigue resistance, ease of melt processing, high purity, and excellent chemical resistance to organics, acids, and bases.Features: Fatigue Resistant; Flame Retardant; Good Chemical Resistance; Good Dimensional Stability; Good Wear Resistance; High Heat ResistanceUses: Aircraft Applications; Bearings; Bushings; Film; Gears; Industrial Applications; Profiles; Rods; Sheet; TubingInjection Molding Notes: Back Pressure: minimumInformation provided by Solvay Specialty Polymers.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.45 g/cc | 0.0524 lb/in³ | ASTM D792 |
| Water Absorption | 0.14 % @Time 86400 sec |
0.14 % @Time 24.0 hour |
ISO 62 |
| Viscosity | 270000 cP @Shear Rate 1000 1/s, Temperature 400 °C |
270000 cP @Shear Rate 1000 1/s, Temperature 752 °F |
Melt Viscosity; ASTM D3835 |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm @Thickness 3.18 mm |
0.0010 - 0.0030 in/in @Thickness 0.125 in |
|
| Linear Mold Shrinkage, Transverse | 0.015 - 0.017 cm/cm @Thickness 3.18 mm |
0.015 - 0.017 in/in @Thickness 0.125 in |
ASTM D955 |
| Melt Flow | 2.4 g/10 min @Load 2.16 kg, Temperature 400 °C |
2.4 g/10 min @Load 4.76 lb, Temperature 752 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 80 | 80 | ASTM D785 |
| Hardness, Shore D | 86 | 86 | 1 sec; ASTM D2240 |
| Tensile Strength | 133 MPa | 19300 psi | ASTM D638 |
| Tensile Strength, Yield | 150 MPa | 21800 psi | 5 mm/min, Type 1A; ISO 527-2 |
| Elongation at Break | 2.8 % | 2.8 % | Type 1A, 5 mm/min; ISO 527-2 |
| 2.8 % | 2.8 % | 5 mm/min; ASTM D638 | |
| Tensile Modulus | 11.0 GPa | 1600 ksi | 5 mm/min; ASTM D638 |
| 14.4 GPa | 2090 ksi | 1 mm/min, Type 1A; ISO 527-2 | |
| Flexural Strength | 218 MPa | 31600 psi | ISO 178 |
| 221 MPa | 32100 psi | ASTM D790 | |
| Flexural Modulus | 10.5 GPa | 1520 ksi | ASTM D790 |
| 14.9 GPa | 2160 ksi | ISO 178 | |
| Compressive Strength | 110 MPa | 16000 psi | ASTM D695 |
| Shear Strength | 70.3 MPa | 10200 psi | ASTM D732 |
| Izod Impact, Notched | 0.690 J/cm | 1.29 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 5.30 J/cm | 9.93 ft-lb/in | ASTM D256 |
| Izod Impact, Notched (ISO) | 9.00 kJ/m² | 4.28 ft-lb/in² | ISO 180 |
| Izod Impact, Unnotched (ISO) | 34.0 kJ/m² | 16.2 ft-lb/in² | ISO 180 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 22.0 µm/m-°C @Temperature -50.0 - 50.0 °C |
12.2 µin/in-°F @Temperature -58.0 - 122 °F |
1 |
| 22.0 µm/m-°C @Temperature -50.0 - 50.0 °C |
12.2 µin/in-°F @Temperature -58.0 - 122 °F |
1 | |
| Specific Heat Capacity | 1.36 J/g-°C @Temperature 50.0 °C |
0.325 BTU/lb-°F @Temperature 122 °F |
ASTM C351 |
| 1.84 J/g-°C @Temperature 200 °C |
0.440 BTU/lb-°F @Temperature 392 °F |
ASTM C351 | |
| Thermal Conductivity | 0.400 W/m-K | 2.78 BTU-in/hr-ft²-°F | ASTM C177 |
| Melting Point | 342 °C | 648 °F | ASTM D3418 |
| Deflection Temperature at 1.8 MPa (264 psi) | 291 °C | 556 °F | Unannealed; ASTM D648 |
| 291 °C | 556 °F | Annealed; ASTM D648 | |
| Glass Transition Temp, Tg | 152 °C | 306 °F | DSC |
| Flammability, UL94 | V-0 @Thickness 0.800 - 1.60 mm |
V-0 @Thickness 0.0315 - 0.0630 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 366 °C | 691 °F | |
| Middle Barrel Temperature | 370 °C | 698 °F | |
| Front Barrel Temperature | 375 °C | 707 °F | |
| Nozzle Temperature | 380 °C | 716 °F | |
| Mold Temperature | 175 - 205 °C | 347 - 401 °F | |
| Drying Temperature | 150 °C @Time 14400 sec |
302 °F @Time 4.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Additive | Carbon Fiber + Graphite + PTFE Lubricant | |
| Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| Latin America | ||
| North America | ||
| Color | Black | |
| Form | Pellets | |
| Injection Rate | Fast | |
| Processing Technique | Injection Molding; Machining; Profile Extrusion | |
| Screw Compression Ratio | 2.5:1.0 to 3.5:1.0 |
Users viewing this material also viewed the following:
- Nye Lubricants UniFlor 8620 (496A) (UF) Synthetic Oil
- Pinnacle Polymers 1517 Polypropylene Homopolymer, Fiber Spinning Grade
- LyondellBasell Plexar® PX3243 Extrudable Tie-Layer Resin, Anhydride Modified LLDPE
- Gouda Vuurvast FLUCON 150 Dense Self Flowing Refractory Castable
- Samsung Cheil Industries Starex® GC-0710 ABS/PET, Unreinforced Recycled
- Teknor Apex Sinvicomp SGH 5500 Polyvinyl Chloride, Flexible
- DuPont Performance Polymers Delrin® 111DP NC010 Acetal (POM) (Unverified Data**)
- Chosun Refractories L12H Magnesia Carbon Bricks for Ladle Slag Line
- 3M 591YT Sandblast Stencil Products
- 3M 2126 Polyethylene Protective Tapes
Copyright © lookpolymers.com All Rights Reserved