Solvay Specialty Polymers KetaSpire® KT-820 GF30 Polyetheretherketone (PEEK), 30% Glass Fiber

Category Polymer , Thermoplastic , Polyketone , Polyetheretherketone (PEEK) , Polyetheretherketone, PEEK, Glass Fiber Filled
Manufacturer Solvay Specialty Polymers
Trade Name KetaSpire®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers KetaSpire® KT-820 GF30 Polyetheretherketone (PEEK), 30% Glass Fiber.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
KetaSpire® KT-820 GF30 is a medium flow, 30% glass fiber reinforced grade of polyetheretherketone (PEEK). This resin offers higher strength and stiffness properties relative to unreinforced KetaSpire® PEEK resin. Reinforcement also affords greater mechanical robustness in structural applications, particularly those with service temperatures approaching 300°C.Features: Autoclave Sterilizable; E-beam Sterilizable; Ethylene Oxide Sterilizable; Fatigue Resistant; Flame Retardant; Good Chemical Resistance; Good Dimensional Stability; Good Sterilizability; Heat Sterilizable; High Heat Resistance; High Stiffness; High Strength; Radiation (Gamma) Resistant; Radiation Sterilizable; Radiotranslucent; Steam Resistant; Steam SterilizableUses: Aircraft Applications; Connectors; Dental Applications; Electrical/Electronic Applications; Film; Hospital Goods; Industrial Applications; Medical Devices; Medical/Healthcare Applications; Oil/Gas Applications; Seals; Surgical InstrumentsInformation provided by Solvay Specialty Polymers.
Physical Properties Metric English Comments
Density 1.53 g/cc
0.0553 lb/in³
ASTM D792
Filler Content 30 %
30 %
Glass Fiber
Water Absorption 0.10 %

@Time 86400 sec
 0.10 %

@Time 24.0 hour
 ISO 62
Viscosity 850000 cP

@Shear Rate 1000 1/s,
Temperature 400 °C
 850000 cP

@Shear Rate 1000 1/s,
Temperature 752 °F
 Melt Viscosity; ASTM D3835
Linear Mold Shrinkage, Flow 0.0020 - 0.0040 cm/cm

@Thickness 3.18 mm
 0.0020 - 0.0040 in/in

@Thickness 0.125 in
Linear Mold Shrinkage, Transverse 0.014 - 0.016 cm/cm

@Thickness 3.18 mm
 0.014 - 0.016 in/in

@Thickness 0.125 in
 ASTM D955
Melt Flow 0.70 g/10 min

@Load 2.16 kg,
Temperature 400 °C
 0.70 g/10 min

@Load 4.76 lb,
Temperature 752 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell M 100
100
ASTM D785
Hardness, Shore D 91
91
1 sec; ASTM D2240
Tensile Strength 158 MPa
22900 psi
ASTM D638
Tensile Strength, Yield 158 MPa
22900 psi
5 mm/min; ASTM D638
165 MPa
23900 psi
5 mm/min, Type 1A; ISO 527-2
Elongation at Break 2.7 %
2.7 %
Nominal; 5 mm/min, Type 1A; ISO 527-2
Tensile Modulus 10.5 GPa
1520 ksi
5 mm/min; ASTM D638
11.4 GPa
1650 ksi
ISO 527-2
Flexural Strength 246 MPa
35700 psi
ISO 178
271 MPa
39300 psi
ASTM D790
Flexural Yield Strength 261 MPa
37900 psi
ASTM D790
Flexural Modulus 10.3 GPa
1490 ksi
ASTM D790
10.7 GPa
1550 ksi
ISO 178
Compressive Strength 169 MPa
24500 psi
ASTM D695
Poissons Ratio 0.34
0.34
ASTM E132
Shear Strength 93.1 MPa
13500 psi
ASTM D732
Izod Impact, Notched 1.10 J/cm
2.06 ft-lb/in
ASTM D256
Izod Impact, Unnotched 9.60 J/cm
18.0 ft-lb/in
ASTM D256
Izod Impact, Notched (ISO) 13.0 kJ/m²
6.19 ft-lb/in²
ISO 180
Izod Impact, Unnotched (ISO) 56.0 kJ/m²
26.6 ft-lb/in²
ISO 180
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 17.0 µm/m-°C

@Temperature -50.0 - 50.0 °C
 9.44 µin/in-°F

@Temperature -58.0 - 122 °F
 1
Specific Heat Capacity 1.30 J/g-°C

@Temperature 50.0 °C
 0.311 BTU/lb-°F

@Temperature 122 °F
 ASTM C351
1.73 J/g-°C

@Temperature 200 °C
 0.413 BTU/lb-°F

@Temperature 392 °F
 ASTM C351
Thermal Conductivity 0.290 W/m-K
2.01 BTU-in/hr-ft²-°F
ASTM C177
Melting Point 340 °C
644 °F
ASTM D3418
Deflection Temperature at 1.8 MPa (264 psi) 315 °C
599 °F
Annealed; ASTM D648
Glass Transition Temp, Tg 150 °C
302 °F
DSC
Flammability, UL94 V-0

@Thickness >=1.60 mm
 V-0

@Thickness >=0.0630 in
Electrical Properties Metric English Comments
Volume Resistivity 1.90e+17 ohm-cm
1.90e+17 ohm-cm
ASTM D257
Surface Resistance >= 1.90e+17 ohm
>= 1.90e+17 ohm
ASTM D257
Dielectric Constant 3.41

@Frequency 1.00e+6 Hz
 3.41

@Frequency 1.00e+6 Hz
 ASTM D150
3.44

@Frequency 60.0 Hz
 3.44

@Frequency 60.0 Hz
 ASTM D150
3.44

@Frequency 1000 Hz
 3.44

@Frequency 1000 Hz
 ASTM D150
Dielectric Strength 17.0 kV/mm

@Thickness 3.00 mm
 432 kV/in

@Thickness 0.118 in
 ASTM D149
Dissipation Factor 0.0010

@Frequency 60.0 Hz
 0.0010

@Frequency 60.0 Hz
 ASTM D150
0.0010

@Frequency 1000 Hz
 0.0010

@Frequency 1000 Hz
 ASTM D150
0.0030

@Frequency 1.00e+6 Hz
 0.0030

@Frequency 1.00e+6 Hz
 ASTM D150
Processing Properties Metric English Comments
Rear Barrel Temperature 365 °C
689 °F
Middle Barrel Temperature 370 °C
698 °F
Front Barrel Temperature 375 °C
707 °F
Nozzle Temperature 380 °C
716 °F
Mold Temperature 175 - 205 °C
347 - 401 °F
Drying Temperature 150 °C

@Time 14400 sec
 302 °F

@Time 4.00 hour
Descriptive Properties Value Comments
Agency Ratings FAA FAR 25.853a; ISO 10993; ISO 10993-Part 1
Availability Africa & Middle East
Asia Pacific
Europe
Latin America
North America
Color Beige
Form Pellets; Powder
Injection Rate Fast
Processing Technique Injection Molding; Machining; Profile Extrusion
RoHS Compliance RoHS Compliant
Screw Compression Ratio 2.5:1.0 to 3.5:1.0