DuPont Performance Polymers Rynite® RE5231 BK533 PET  (Unverified Data**)

Category Polymer , Renewable/Recycled Polymer , Thermoplastic , Polyester, TP , Polyethylene Terephthalate (PET) , Polyethylene Terephthalate (PET), Recycled, Glass/Mineral Reinforced
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Rynite® RE5231 BK533 PET  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Rynite® RE5231 BK533 is a 35% glass fiber/mica reinforced product modified for improved electrical properties such as dielectric strength.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Specific Gravity 1.60 g/cc
1.60 g/cc
ASTM D792
Linear Mold Shrinkage 0.0030 cm/cm

@Thickness 3.20 mm
0.0030 in/in

@Thickness 0.126 in
Flow
0.0090 cm/cm

@Thickness 3.20 mm
0.0090 in/in

@Thickness 0.126 in
Transverse
Mechanical Properties Metric English Comments
Tensile Strength at Break 94.0 MPa

@Temperature 23.0 °C
13600 psi

@Temperature 73.4 °F
ISO 527
Tensile Strength 94.0 MPa

@Temperature 23.0 °C
13600 psi

@Temperature 73.4 °F
ASTM D638
Elongation at Break 2.0 %

@Temperature 23.0 °C
2.0 %

@Temperature 73.4 °F
ASTM D638
2.0 %

@Temperature 23.0 °C
2.0 %

@Temperature 73.4 °F
ISO 527
Flexural Strength 147 MPa

@Temperature 23.0 °C
21300 psi

@Temperature 73.4 °F
ASTM D790
Flexural Modulus 9.60 GPa

@Temperature 23.0 °C
1390 ksi

@Temperature 73.4 °F
ASTM D790
Izod Impact, Notched 0.590 J/cm

@Temperature 23.0 °C
1.11 ft-lb/in

@Temperature 73.4 °F
ASTM D256
Izod Impact, Unnotched 5.00 J/cm

@Temperature 23.0 °C
9.37 ft-lb/in

@Temperature 73.4 °F
ASTM D4812
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 216 °C
421 °F
ISO 75-1/-2
216 °C
421 °F
ASTM D648
Flammability, UL94 HB

@Thickness 0.750 mm
HB

@Thickness 0.0295 in
IEC 60695-11-10
HB

@Thickness 0.750 mm
HB

@Thickness 0.0295 in
UL94
Electrical Properties Metric English Comments
Dielectric Strength 13.8 kV/mm

@Thickness 3.20 mm,
Temperature 200 °C
351 kV/in

@Thickness 0.126 in,
Temperature 392 °F
Short Time; ASTM D149
25.6 kV/mm

@Thickness 3.20 mm,
Temperature 120 °C
650 kV/in

@Thickness 0.126 in,
Temperature 248 °F
Short Time; ASTM D149
>= 28.0 kV/mm

@Thickness 3.20 mm,
Temperature 23.0 °C
>= 711 kV/in

@Thickness 0.126 in,
Temperature 73.4 °F
Short Time; ASTM D149
Processing Properties Metric English Comments
Melt Temperature 280 - 300 °C
536 - 572 °F
Mold Temperature >= 95.0 °C
>= 203 °F
Drying Temperature 120 °C
248 °F
Dry Time 4.00 hour
4.00 hour
Moisture Content <= 0.020 %
<= 0.020 %
Descriptive Properties Value Comments
Appearance Black Color
Drying Recommended Yes
Features Dimensional Stability, Good
Electrical Properties, Good
Stiffness, Good
Strength, Good
Thermal Aging Resistance, Good
Warp Resistant
Filler Glass/Mica
Forms Pellets
Generic PET
Heat Stabilized Yes
Material Status Current
Part Marking Code >PET-(GF+MD)35<
ISO 11469
Polymer Family Polyester
Polymer Type PET
Processing Method Injection Molding
Product Category Electrical Resins
Glass/Mineral Reinforced Resins
Low Warp Resins
Resin Identification PET-(GF+MD)35
ISO 1043
RoHS Compliance Contact Manufacturer
Ultrasonic Weldable Yes
Uses Automotive Applications
Electrical Parts
Electrical/Electronic Applications
Housings
Phenolic Replacement
Structural Parts