Solvay Specialty Polymers AvaSpire® AV-621 CF30 Polyaryletherketone (PAEK)  (Unverified Data**)

Category Polymer , Thermoplastic , Polyketone , Polyaryletherketone (PAEK), Carbon Fiber Filled
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Solvay Specialty Polymers AvaSpire® AV-621 CF30 Polyaryletherketone (PAEK)  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
AvaSpire AV-621 CF30 is a 30% carbon fiber reinforced version of AvaSpire AV-621. It offers better dimensional stability and warp resistance than 30% carbon fiber reinforced PEEK. The AV-621 CF30 grade offers the highest strength, stiffness, and fatigue resistance of any AV-621 based grade. Furthermore, this resin generally retains most of the desirable ultra-performance attributes of carbon fiber reinforced PEEK including chemical resistance, fatigue resistance, and long term thermal oxidative stability. The excellent balance of properties of AV-621 CF30 makes this grade well suited for a broad range of applications across a number of industries, including healthcare, transportation, electronics, and chemical processing. This resin can be easily melt processed by injection molding using standard equipment. The melt processing behavior of AV-621 CF30 is very similar to that of 30% CF reinforced PEEK. The lower melt flow of AV-621 CF30 is well suited for extrusion applications while offering a similar property profile to AV-651 CF30.Injection Notes: Back Pressure: MinimumInformation provided by Solvay Specialty Polymers.
Physical Properties Metric English Comments
Specific Gravity 1.42 g/cc
1.42 g/cc
ASTM D792
Filler Content 30 %
30 %
Carbon Fiber Reinforcement
Water Absorption 0.10 %

@Time 86400 sec
0.10 %

@Time 24.0 hour
ASTM D570
Viscosity 790000 cP

@Shear Rate 1000 1/s,
Temperature 400 °C
790000 cP

@Shear Rate 1000 1/s,
Temperature 752 °F
Melt; ASTM D3835
Linear Mold Shrinkage, Flow 0.00 - 0.0020 cm/cm

@Thickness 3.18 mm
0.00 - 0.0020 in/in

@Thickness 0.125 in
5" x 0.5" x 0.125" bars; ASTM D955
Linear Mold Shrinkage, Transverse 0.0090 - 0.011 cm/cm

@Thickness 3.18 mm
0.0090 - 0.011 in/in

@Thickness 0.125 in
5" x 0.5" x 0.125" bars; ASTM D955
Melt Flow 1.0 g/10 min

@Load 2.16 kg,
Temperature 400 °C
1.0 g/10 min

@Load 4.76 lb,
Temperature 752 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell M 101
101
M-Scale; ASTM D785
Tensile Strength 181 MPa
26300 psi
5.0 mm/min; ASTM D638
Tensile Strength, Yield 196 MPa
28400 psi
ISO 527-2/1A/5
Elongation at Break 2.2 %
2.2 %
5.0 mm/min; ASTM D638
2.2 %
2.2 %
ISO 527-2/1A/5
Tensile Modulus 17.2 GPa
2490 ksi
5.0 mm/min; ASTM D638
23.3 GPa
3380 ksi
ISO 527-2/1A/1
Flexural Strength 276 MPa
40000 psi
ASTM D790
296 MPa
42900 psi
ISO 178
Flexural Modulus 15.1 GPa
2190 ksi
ASTM D790
21.3 GPa
3090 ksi
ISO 178
Compressive Strength 152 MPa
22000 psi
ASTM D695
Shear Strength 91.0 MPa
13200 psi
ASTM D732
Izod Impact, Notched 0.690 J/cm
1.29 ft-lb/in
ASTM D256
6.40 J/cm
12.0 ft-lb/in
ASTM D4812
Izod Impact, Notched (ISO) 9.60 kJ/m²
4.57 ft-lb/in²
ISO 180
Izod Impact, Unnotched (ISO) 39.0 kJ/m²
18.6 ft-lb/in²
ISO 180
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 5.00 µm/m-°C

@Temperature -50.0 - 50.0 °C
2.78 µin/in-°F

@Temperature -58.0 - 122 °F
TMA; ASTM E831
Specific Heat Capacity 1.35 J/g-°C

@Temperature 50.0 °C
0.323 BTU/lb-°F

@Temperature 122 °F
DSC
1.81 J/g-°C

@Temperature 200 °C
0.433 BTU/lb-°F

@Temperature 392 °F
DSC
Thermal Conductivity 0.350 W/m-K
2.43 BTU-in/hr-ft²-°F
ASTM E1530
Melting Point 340 °C
644 °F
Peak; ASTM D3418
Deflection Temperature at 1.8 MPa (264 psi) 210 °C

@Thickness 3.20 mm
410 °F

@Thickness 0.126 in
Annealed; 2 hours at 200°C; ASTM D648
Glass Transition Temp, Tg 160 °C
320 °F
ASTM D3418
Processing Properties Metric English Comments
Rear Barrel Temperature 366 °C
691 °F
Middle Barrel Temperature 371 °C
700 °F
Front Barrel Temperature 377 °C
711 °F
Nozzle Temperature 382 °C
720 °F
Melt Temperature 366 - 388 °C
691 - 730 °F
Mold Temperature 149 - 177 °C
300 - 351 °F
Drying Temperature 149 °C
300 °F
Dry Time 4.00 hour
4.00 hour
Descriptive Properties Value Comments
Appearance Black
Availability Africa & Middle East
Asia Pacific
Europe
North America
South America
Features Fatigue Resistant
Flame Retardant
Good Chemical Resistance
Good Dimensional Stability
High Heat Resistance
High Stiffness
High Strength
Forms Pellets
Generic PAEK
Injection Rate Fast
Processing Method Injection Molding
Machining
Profile Extrusion
Screw Compression Ratio 2.0:1.0 to 3.0:1.0
Uses Medical/Healthcare Applications
Pump Parts