A. Schulman POLYPUR™ FPU 1380 Thermoplastic Polyurethane Compound
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Molded , Polyurethane, TP |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | A. Schulman POLYPUR™ FPU 1380 Thermoplastic Polyurethane Compound.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by A. Schulman.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.18 g/cc | 1.18 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0010 - 0.0030 cm/cm @Thickness 3.20 mm |
0.0010 - 0.0030 in/in @Thickness 0.126 in |
72 hr; ASTM D955 |
| 0.0020 - 0.0040 cm/cm @Thickness 3.20 mm |
0.0020 - 0.0040 in/in @Thickness 0.126 in |
48 hr at 80°C; ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 67 | 67 | ASTM D2240 |
| Tensile Strength at Break | 30.0 MPa | 4350 psi | 2 in/min; ASTM D638 |
| Elongation at Break | 15 % | 15 % | 2 in/min; ASTM D412 |
| Flexural Modulus | 0.900 GPa | 131 ksi | 1.3 mm/min at 70°C |
| 1.38 GPa | 200 ksi | 1.3 mm/min; ASTM D790 | |
| Izod Impact, Notched | 2.15 J/cm | 4.03 ft-lb/in | ASTM D256 |
| Tear Strength | 100 kN/m | 571 pli | 2 in/min; ASTM D624 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 215 °C | 419 °F | DSC 10°C/min |
| Deflection Temperature at 0.46 MPa (66 psi) | 85.0 °C | 185 °F | ASTM D648 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Heat Sag | 8 mm | ASTM D3769, 1 hr at 80°C, 6 in. overhang |
Users viewing this material also viewed the following:
- Niche Polymer PPCM15BK Copolymer PP
- Performance Alloys MoldStar® 18 (PAS 18) Bronze Mold Alloy
- PolyOne Geon™ Vinyl Flexible B87FB Polyvinyl Chloride, Flexible (PVC, Flexible)
- Malvern Minerals Sliastic 740 with 33% Novacite® Daper Quartz Filler
- Stir SpA C 2036 DS AT (PVC)
- A. Schulman POLYTROPE™ TPP 530 Injection Molding Grade Olefinic Thermoplastic Elastomer
- A. Schulman POLYPUR™ FPU 1117 Thermoplastic Polyurethane Compound
- Ensinger Tecapeek® XP-104 Compression Molded PEEK Compound, with 7% Molybdenum Disulfide, 3% PTFE and 25% Carbon Fiber
- Duratherm 630 Paraffinic Heat Transfer Fluid
- Colorite Polymers 7011-Rad Radiopaque Vinyl Compound
Copyright © lookpolymers.com All Rights Reserved