- Solvay Specialty Polymers Amodel® A-1145 HS Polyphthalamide (PPA), 45% Glass Fiber (Dry)
Solvay Specialty Polymers Amodel® A-1145 HS Polyphthalamide (PPA), 45% Glass Fiber (Dry)
| Category | Polymer , Thermoplastic , Polyphthalamide (PPA) , Polyphthalamide (PPA), 50% Glass Fiber Reinforced |
| Manufacturer | Solvay Specialty Polymers |
| Trade Name | Amodel® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Solvay Specialty Polymers Amodel® A-1145 HS Polyphthalamide (PPA), 45% Glass Fiber (Dry).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Amodel® A-1145 HS is a 45% glass reinforced, heat stabilized polyphthalamide (PPA) with a high heat deflection temperature, very high flexural modulus and very high tensile strength. Excellent creep resistance and low moisture absorption are also characteristic of this resin.Features: Good Chemical Resistance; Good Creep Resistance; Good Dimensional Stability; Good Stiffness; High Heat Resistance; High Strength; High Temperature Strength; Low Moisture AbsorptionUses: Automotive Applications; Automotive Electronics; Automotive Under the Hood; Connectors; Housings; Industrial Applications; Industrial Parts; Machine/Mechanical Parts; Metal Replacement; Power/Other Tools; Valves/Valve PartsInjection Molding Notes: Amodel® compounds are shipped in moisture-resistant packages at moisture levels according to specifications. Sealed, undamaged bags should be preferably stored in a dry room at a maximum temperature of 50°C (122°F) and should be protected from possible damage. If only a portion of a package is used, the remaining material should be transferred into a sealable container. It is recommended that Amodel® resins be dried prior to molding.Automotive Specifications 3M 11-0003-5762-1 Color: BK324 Black; ASTM D4000 PA121 G45 Color: BK324 Black; ASTM D4000 PA121 G45 Color: NT Natural; ASTM D4000 PPA0120 G46 A95726 AA002 CD295 GB159 MF015Z Color: BN575 Brown; ASTM D6779 PA121G45; BOSCH 9 916 365 011 Color: BK 324 Black; BOSCH 9 916 365 011 Color: NT Natural; CHRYSLER MS-DB-478 Type B CPN3567 Color: Black; FORD WSB-M4D861-A Color: BK324 Black; FORD WSB-M4D861-A Color: NT Natural; GM GMP.PPA.008 Color: BK324 Black; GM GMP.PPA.008 Color: NT Natural; GM GMW16356P-PPA-GF45 Color: BK-324 Black; GM GMW16356P-PPA-GF45 Color: NT Natural; ISO 1874 PA6T/6I/66, MH, 12-160, GF45 Color: NT Natural; TRW S-13301201 Color: BK324 BlackInformation provided by Solvay Specialty Polymers.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.59 g/cc | 0.0574 lb/in³ | ISO 1183 |
| Filler Content | 45 % | 45 % | Glass Fiber |
| Water Absorption | 0.12 % @Time 86400 sec |
0.12 % @Time 24.0 hour |
ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm | 0.0020 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0060 cm/cm | 0.0060 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 125 | 125 | ASTM D785 |
| Tensile Strength at Break | 75.8 MPa @Temperature 175 °C |
11000 psi @Temperature 347 °F |
4; ISO 527-2 |
| 84.8 MPa @Temperature 150 °C |
12300 psi @Temperature 302 °F |
4; ISO 527-2 | |
| 173 MPa @Temperature 100 °C |
25100 psi @Temperature 212 °F |
4; ISO 527-2 | |
| 263 MPa @Temperature 23.0 °C |
38100 psi @Temperature 73.4 °F |
4; ISO 527-2 | |
| Tensile Strength | 259 MPa | 37600 psi | ASTM D638 |
| Elongation at Break | 2.6 % | 2.6 % | ASTM D638 |
| 2.5 % @Temperature 100 °C |
2.5 % @Temperature 212 °F |
ISO 527-2 | |
| 2.7 % @Temperature 23.0 °C |
2.7 % @Temperature 73.4 °F |
ISO 527-2 | |
| 6.5 % @Temperature 175 °C |
6.5 % @Temperature 347 °F |
ISO 527-2 | |
| 7.2 % @Temperature 150 °C |
7.2 % @Temperature 302 °F |
ISO 527-2 | |
| Tensile Modulus | 17.2 GPa | 2490 ksi | ASTM D638 |
| 5.38 GPa @Temperature 175 °C |
780 ksi @Temperature 347 °F |
4; ISO 527-2 | |
| 8.00 GPa @Temperature 150 °C |
1160 ksi @Temperature 302 °F |
4; ISO 527-2 | |
| 11.2 GPa @Temperature 100 °C |
1620 ksi @Temperature 212 °F |
4; ISO 527-2 | |
| 16.8 GPa @Temperature 23.0 °C |
2440 ksi @Temperature 73.4 °F |
4; ISO 527-2 | |
| Flexural Strength | 363 MPa | 52600 psi | ASTM D790 |
| 94.5 MPa @Temperature 175 °C |
13700 psi @Temperature 347 °F |
4; ISO 178 | |
| 111 MPa @Temperature 150 °C |
16100 psi @Temperature 302 °F |
4; ISO 178 | |
| 267 MPa @Temperature 100 °C |
38700 psi @Temperature 212 °F |
4; ISO 178 | |
| 377 MPa @Temperature 23.0 °C |
54700 psi @Temperature 73.4 °F |
4; ISO 178 | |
| Flexural Modulus | 13.8 GPa | 2000 ksi | ASTM D790 |
| 4.90 GPa @Temperature 175 °C |
711 ksi @Temperature 347 °F |
ISO 178 | |
| 5.38 GPa @Temperature 150 °C |
780 ksi @Temperature 302 °F |
ISO 178 | |
| 13.0 GPa @Temperature 100 °C |
1890 ksi @Temperature 212 °F |
ISO 178 | |
| 15.9 GPa @Temperature 23.0 °C |
2310 ksi @Temperature 73.4 °F |
ISO 178 | |
| Compressive Strength | 194 MPa @Thickness 25.4 mm |
28100 psi @Thickness 1.00 in |
ASTM D695 |
| Poissons Ratio | 0.41 | 0.41 | ASTM E132 |
| Shear Strength | 108 MPa | 15700 psi | ASTM D732 |
| Izod Impact, Notched | 1.10 J/cm | 2.06 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 11.0 J/cm | 20.6 ft-lb/in | ASTM D256 |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² | 4.76 ft-lb/in² | Type 1, Notch A; ISO 180 |
| Izod Impact, Unnotched (ISO) | 61.0 kJ/m² | 29.0 ft-lb/in² | Type 1; ISO 180 |
| Charpy Impact Unnotched | 9.20 J/cm² | 43.8 ft-lb/in² | Type 1, Edgewise; ISO 179 |
| Charpy Impact, Notched | 1.00 J/cm² | 4.76 ft-lb/in² | Type 1, Edgewise; ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 14.0 µm/m-°C @Temperature 0.000 - 100 °C |
7.78 µin/in-°F @Temperature 32.0 - 212 °F |
2 |
| 35.0 µm/m-°C @Temperature 100 - 200 °C |
19.4 µin/in-°F @Temperature 212 - 392 °F |
2 | |
| CTE, linear, Transverse to Flow | 50.0 µm/m-°C @Temperature 0.000 - 100 °C |
27.8 µin/in-°F @Temperature 32.0 - 212 °F |
TMA; ASTM E831 |
| 150 µm/m-°C @Temperature 100 - 200 °C |
83.3 µin/in-°F @Temperature 212 - 392 °F |
TMA; ASTM E831 | |
| Melting Point | 310 °C | 590 °F | ASTM D3418 |
| 310 °C | 590 °F | ISO 11357-3 | |
| Maximum Service Temperature, Air | 165 - 185 °C | 329 - 365 °F | Continuous Use |
| Deflection Temperature at 0.46 MPa (66 psi) | 301 °C @Thickness 3.20 mm |
574 °F @Thickness 0.126 in |
Annealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 281 °C | 538 °F | Unannealed; ISO 75-2/A |
| 287 °C @Thickness 3.20 mm |
549 °F @Thickness 0.126 in |
Annealed; ASTM D648 | |
| Flammability, UL94 | HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Dielectric Constant | 4.4 @Frequency 1.00e+6 Hz |
4.4 @Frequency 1.00e+6 Hz |
ASTM D150 |
| 4.6 @Frequency 60.0 Hz |
4.6 @Frequency 60.0 Hz |
ASTM D150 | |
| Dielectric Strength | 23.0 kV/mm @Thickness 3.20 mm |
584 kV/in @Thickness 0.126 in |
ASTM D149 |
| Dissipation Factor | 0.0050 @Frequency 60.0 Hz |
0.0050 @Frequency 60.0 Hz |
ASTM D150 |
| 0.016 @Frequency 1.00e+6 Hz |
0.016 @Frequency 1.00e+6 Hz |
ASTM D150 | |
| Arc Resistance | 145 sec | 145 sec | ASTM D495 |
| Comparative Tracking Index | 550 V | 550 V | UL 746 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 304 - 318 °C | 579 - 604 °F | |
| Front Barrel Temperature | 316 - 329 °C | 601 - 624 °F | |
| Melt Temperature | 321 - 343 °C | 610 - 649 °F | |
| Mold Temperature | 135 °C | 275 °F | |
| Drying Temperature | 120 °C @Time 16200 sec |
248 °F @Time 4.50 hour |
|
| Moisture Content | <= 0.045 % | <= 0.045 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Additive | Heat Stabilizer | |
| Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| Latin America | ||
| North America | ||
| Color | Black; Natural | |
| Form | Pellets | |
| Processing Technique | Injection Molding | |
| RoHS Compliance | RoHS Compliant |
Users viewing this material also viewed the following:
- Chevron Phillips 5497 LDPE High Clarity, Bakery Packaging Film Resin (discontinued **)
- Haynes Hastelloy® C-22® alloy, 40% cold worked sheet
- American Elements Iron Cobalt Nanopowder
- Dow Corning 1665 EMULSION
- EMS-Grivory Grivory® HT1V-3 FWA black 9225 PA6T/6I-GF30
- Azdel SuperLite® SL551800-100 PP Resin Matrix / 55% Glass Fiber (8 mm Molded Thickness)
- Arlon 49581X010 0.0105" (0.267 mm) Uncured Silicone Rubber with Fiberglass Substrate
- AK Steel ASTM A 607 Class 2 Formable, Grade 45K Hot Rolled Carbon Steel, Medium/High Strength Low Alloy (HSLA)
- Fainplast Compounds PM 80/A Flexible PVC, Lead Free
Copyright © lookpolymers.com All Rights Reserved