- Sichuan Deyang Haton® hGR30 Polyphenylene Sulfide, Glass Fiber Reinforced
Sichuan Deyang Haton® hGR30 Polyphenylene Sulfide, Glass Fiber Reinforced
| Category | Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) , Polyphenylene Sulfide (PPS) with 30% Glass Fiber Filler |
| Manufacturer | Sichuan Deyang Chemical Co. Ltd. |
| Trade Name | Haton® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Sichuan Deyang Haton® hGR30 Polyphenylene Sulfide, Glass Fiber Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Injection moldingInformation provided by Sichuan Deyang Chemical Co., LTD
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.55 g/cc | 0.0560 lb/in³ | GB/T 1033.1-2008 |
| Water Absorption | 0.020 % | 0.020 % | GB/T 1034-2008 |
| Linear Mold Shrinkage, Flow | 0.0025 cm/cm | 0.0025 in/in | GB/T 15585-1995 |
| Linear Mold Shrinkage, Transverse | 0.0075 cm/cm | 0.0075 in/in | GB/T 15585-1995 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell L | 106 | 106 | GB/T 3398.2-2008 |
| Tensile Strength | 167 MPa | 24200 psi | GB/T 1040.2-2006 |
| Elongation at Break | 1.9 % | 1.9 % | GB/T1040.2-2006 |
| Flexural Strength | 242 MPa | 35100 psi | GB/T 9341-2008 |
| Flexural Modulus | 11.9 GPa | 1730 ksi | GB/T 9341-2008 |
| Izod Impact, Notched (ISO) | 14.0 kJ/m² | 6.66 ft-lb/in² | GB/T 1843-2008 |
| Izod Impact, Unnotched (ISO) | 52.0 kJ/m² | 24.7 ft-lb/in² | GB/T 1843-2008 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 280 °C | 536 °F | GBT/T 19466.3-2004 |
| Deflection Temperature at 1.8 MPa (264 psi) | 268 °C | 514 °F | GB/T 1634.2-2004 |
| Flammability, UL94 | V-0 | V-0 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 2.40e+16 ohm-cm | 2.40e+16 ohm-cm | GB/T1410-2006 |
| Surface Resistivity per Square | 5.60e+15 ohm | 5.60e+15 ohm | GB/T1410-2006 |
| Dielectric Constant | 3.2 | 3.2 | GB/T 1409-2006 |
| Dielectric Strength | 16.0 kV/mm | 406 kV/in | GB/T1408.1-2006 |
| Dissipation Factor | 0.0020 | 0.0020 | GB/T 1409-2006 |
Users viewing this material also viewed the following:
- MetalTek MTEK 115 Martensitic Stainless Steel
- Solvay Specialty Polymers Catalyst CT/1 Polyolefin
- Plenco 2308 Phenolic, Granular, Injection Molded
- Toyobo GLAMIDE® T-403 Nylon-6
- Zircar Refractory Composites RS-DA Refractory Sheet
- Elmer's Products Aron Alpha® 432TB Cyanoacrylate Adhesive (Industrial Krazy Glue™)
- 3M 9674 Adhesive Transfer Tapes with Adhesive 300
- BASF Ultramid® A3WG7 35% Glass Filled PA66 (Dry)
Copyright © lookpolymers.com All Rights Reserved