Dow Elite® 5110 Linear Low Density Polyethylene
| Category | Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Film Grade |
| Manufacturer | Dow Chemical |
| Trade Name | Elite® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Dow Elite® 5110 Linear Low Density Polyethylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
5110 enhanced polyethylene resin is a copolymer produced via INSITE Technology from Dow Plastics. It offers unique combination of high modulus and excellent impact strength, allowing for downgauging in bag applications. In addition, 5110 resin has excellent tensile strength and good tear properties. It complies with U.S. FDA regulation 21 CFR 177.1520 c 3.2 (a) when used unmodified and processed according to good manufacturing practices. For food contact compliance statements, your nearest Dow office should be contacted.Data provided by Dow Chemical.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.926 g/cc | 0.0335 lb/in³ | |
| Melt Flow | 0.85 g/10 min @Load 2.16 kg |
0.85 g/10 min @Load 4.76 lb |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Yield, MD | 14.0 MPa | 2030 psi | |
| Film Tensile Strength at Yield, TD | 15.0 MPa | 2180 psi | |
| Film Elongation at Break, MD | 615 % | 615 % | |
| Film Elongation at Break, TD | 640 % | 640 % | |
| Secant Modulus, MD | 0.228 GPa | 33.1 ksi | Film value |
| Secant Modulus, TD | 0.2485 GPa | 36.04 ksi | Film value |
| Elmendorf Tear Strength MD | 750 g | 750 g | Unspecified film thickness |
| Elmendorf Tear Strength TD | 1150 g | 1150 g | Unspecified film thickness |
| Dart Drop Test | 400 g | 0.882 lb | |
| Film Tensile Strength at Break, MD | 51.4 MPa | 7450 psi | |
| Film Tensile Strength at Break, TD | 44.5 MPa | 6450 psi |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Vicat Softening Point | 113 °C | 235 °F |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 13 % | 13 % |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 111 °C | 232 °F | Seal Initiation temperature |
Users viewing this material also viewed the following:
- Multibase SILASTIC® Type A Dow-Corning Medical Adhesive Silicone
- Overview of materials for Acetal Homopolymer, Unreinforced, Impact Grade
- NOVA Chemicals Dylark® 480P20 High Performance Glass Filled Styrenic
- Total Finathene® SR 572 HDPE blow molding (discontinued **)
- Metabolix Mirelâ„¢ I6003rp Biobased PHA Polymeric Modifier
- Sax Polymers SAXAMID 226F6RY01 Nylon 6.6, 30% Glass Fiber
- Teknor Apex Tekbond® TB 2006 Thermoplastic Elastomer
- Fainplast Compounds HAX HF 4121 Halogen Free PVC
- 3M 12050 Black 1/2" (12.7 mm) Polyurethane Foam
- Fainplast Compounds Hax™ HF 045/11 Flame Retardant Polyolefin Cable Compound
Copyright © lookpolymers.com All Rights Reserved