Shinkong Synthetic Fibers Shinite® D201 PBT
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Shinkong Synthetic Fibers Shinite® D201 PBT.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information from Shinkong Synthetic Fibers Corp.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.31 g/cc | 1.31 g/cc | ASTM D792 |
| Water Absorption | 0.090 % | 0.090 % | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0080 - 0.020 cm/cm | 0.0080 - 0.020 in/in | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0080 - 0.020 cm/cm | 0.0080 - 0.020 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 53.9 MPa | 7820 psi | ASTM D638 |
| Elongation at Break | 40 % | 40 % | ASTM D638 |
| Flexural Yield Strength | 83.4 MPa | 12100 psi | ASTM D790 |
| Flexural Modulus | 2.45 GPa | 356 ksi | ASTM D790 |
| Izod Impact, Notched | 0.392 J/cm @Thickness 3.17 mm, Temperature 23.0 °C |
0.735 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 65.0 °C | 149 °F | ASTM D648 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.0 | 3.0 | ASTM D150 |
| Dielectric Strength | 15.0 kV/mm | 381 kV/in | ASTM D149 |
Users viewing this material also viewed the following:
- Resinlab® CYNERGY CA6906 Adhesive
- PolyOne Geon™ Vinyl Rigid Extrusion 87548 AS Polyvinyl Chloride, Rigid (PVC, Rigid)
- Polymax® Maxelast® N8955 TPE, Nylon Overmold
- Parker Chomerics CHO-MASK II ST Conductive Foil Tape
- Samsung Cheil Industries Infino® FD-1112 PC, FR
- A. Schulman POLYBATCH™ Blue Tint P40530 Concentrate Based In Homopolymer Polypropylene
- TSE Industries Millathane® 5004 Millable Polyurethane Elastomer with 20 PHR HAF Black (Typical)
- Compuestos Dominicanos Polycom BD-320699 PVC Compound
Copyright © lookpolymers.com All Rights Reserved