ExxonMobil LL 1107x93 Blown Film Resin

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Film Grade
Manufacturer Exxon Chemical
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF ExxonMobil LL 1107x93 Blown Film Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description: LL 1107 resins are fractional melt index butane LLDPE blown film resins. Films made with LL 1107 resins have good stiffness and tensile strength. Theses resins’ strength and drawability make them excellent for many film applications. Availability: Latin America, North America and South America Additive: Antiblock: 3500 ppmSlip: 1000 ppmProcessing Aid: Yes Thermal Stabilizer: YesApplications: Blown FilmGarment FilmProduce Bags Information provided by ExxonMobil Chemical
Physical Properties Metric English Comments
Density 0.922 g/cc
0.0333 lb/in³
ExxonMobil Method
Melt Flow 0.80 g/10 min

@Load 2.16 kg,
Temperature 190 °C
0.80 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Antiblock Level 3500 ppm
3500 ppm
Slip Level 1000 ppm
1000 ppm
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 10.2 MPa
1480 psi
ASTM D882
Film Tensile Strength at Yield, TD 11.0 MPa
1600 psi
ASTM D882
Film Elongation at Break, MD 520 %
520 %
ASTM D882
Film Elongation at Break, TD 690 %
690 %
ASTM D882
Puncture Energy 1.05 J
0.775 ft-lb
ExxonMobil
Elmendorf Tear Strength, MD 2.76 g/micron
70.0 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 17.3 g/micron
440 g/mil
ASTM D1922
Dart Drop 2.36 g/micron
60.0 g/mil
ASTM D1709
Film Tensile Strength at Break, MD 45.8 MPa
6640 psi
ASTM D882
Film Tensile Strength at Break, TD 27.2 MPa
3940 psi
ASTM D882
1% Secant Modulus, MD 230 MPa
33400 psi
ASTM D882
1% Secant Modulus, TD 261 MPa
37800 psi
ASTM D882
Thermal Properties Metric English Comments
Melting Point 123 °C
253 °F
Peak Melting Temperature; ExxonMobil Method
Optical Properties Metric English Comments
Haze 18.4 %
18.4 %
ASTM D1003
Gloss 46 %
46 %
45°; ASTM D2457
Descriptive Properties Value Comments
Features Thermal Stabilizer