Schwartz Technical Plastics LAMIGAMID® 410 Cast Polyamide 6, Elastomer Modified, Low Temp, Dry
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Cast |
| Manufacturer | Schwartz Technical Plastics |
| Trade Name | LAMIGAMID® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Schwartz Technical Plastics LAMIGAMID® 410 Cast Polyamide 6, Elastomer Modified, Low Temp, Dry.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Application: outrigger floats, rollersInformation provided by Schwartz Technical Plastics GmbH
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.11 g/cc | 0.0401 lb/in³ | ISO R 1183 |
| Moisture Absorption at Equilibrium | 2.3 % | 2.3 % | DIN 53473 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 70.0 MPa | 10200 psi | Hc 30; ISO 2039; partially |
| Tensile Strength, Yield | 40.0 MPa | 5800 psi | ISO-DIS 527 |
| Tensile Modulus | 1.50 GPa | 218 ksi | DIN 53457 |
| Flexural Strength | 20.0 MPa | 2900 psi | DIN 54352 |
| Flexural Modulus | 1.30 GPa | 189 ksi | DIN 53457 |
| Izod Impact, Notched (ISO) | 45.0 kJ/m² | 21.4 ft-lb/in² | ISO 180-1A |
| Izod Impact Resistance | NB | NB | swinging hammer 0,1 DIN 51222; DIN 53453 |
| Tear Strength Test | >= 1.8 | >= 1.8 | ISO-DIS 527 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 100 - 180 µm/m-°C @Temperature 20.0 - 100 °C |
55.6 - 100 µin/in-°F @Temperature 68.0 - 212 °F |
DIN 53752 |
| Melting Point | 205 °C | 401 °F | ISO R 1218 |
| Maximum Service Temperature, Air | 60.0 °C | 140 °F | Continuous |
| Deflection Temperature at 0.46 MPa (66 psi) | 160 °C | 320 °F | V-notch; ISO R 75 |
| Minimum Service Temperature, Air | -50.0 °C | -58.0 °F | Continuous |
Users viewing this material also viewed the following:
- PolyOne Dynaflex™ G7970-1001-00 Thermoplastic Elastomer (TPE)
- Momentive Performance Materials Siloprenâ„¢ LIM 6010 Liquid Silicone Rubber - Fast Cure / High Tear
- Karina 920-10/156-Y-IS-BZ White PVC Compound
- Less Common Metals SmCo5 Samarium Cobalt Alloy; Vacuum Induction Melting & Casting
- Haynes 214® alloy, 30% cold reduction, 980°C (1800°F) for 5 minutes
- Solvay RHODAFAC® LO/529-E Surfactant
- Styrolution Absolan® 2300 Sparkle SAN
- A. Schulman PP 1277A-01 Polypropylene High-Impact Polypropylene
- Adell RZ-16 Copolymer Polypropylene, 30% Calcium Carbonate Filled
Copyright © lookpolymers.com All Rights Reserved