- Sax Polymers SAXAMID 226F4RY01 Nylon 6.6, 20% Glass Fiber
Sax Polymers SAXAMID 226F4RY01 Nylon 6.6, 20% Glass Fiber
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 20% Glass Fiber Filled , Nylon 66, Glass Fiber Filled, Flame Retardant |
| Manufacturer | Sax Polymers |
| Trade Name | SAXAMID |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Sax Polymers SAXAMID 226F4RY01 Nylon 6.6, 20% Glass Fiber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
SAXAMID 226F4RY01 is a polyamide 6.6 injection-molding-grade reinforced with 20% glass fibers. It has a halogen-free flame retardant.Information provided by SAX Polymers
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.31 g/cc | 0.0473 lb/in³ | ISO 1183 |
| Viscosity Test | 150 cm³/g | 150 cm³/g | H<sub>2</sub>SO<sub>4</sub>; ISO 307 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 118 MPa | 17100 psi | 5 mm/min; ISO 527-1 |
| Elongation at Break | 2.5 % | 2.5 % | 5 mm/min; ISO 527-1 |
| Tensile Modulus | 8.30 GPa | 1200 ksi | 1 mm/min; ISO 527-1 |
| Flexural Strength | 180 MPa | 26100 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 6.70 GPa | 972 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 6.50 kJ/m² @Temperature -30.0 °C |
3.09 ft-lb/in² @Temperature -22.0 °F |
ISO 180/1A |
| 7.00 kJ/m² @Temperature 23.0 °C |
3.33 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | 39.0 kJ/m² @Temperature -30.0 °C |
18.6 ft-lb/in² @Temperature -22.0 °F |
ISO 180/1U |
| 45.0 kJ/m² @Temperature 23.0 °C |
21.4 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1U | |
| Charpy Impact Unnotched | 4.60 J/cm² @Temperature -30.0 °C |
21.9 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eU |
| 5.70 J/cm² @Temperature 23.0 °C |
27.1 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 0.550 J/cm² @Temperature -30.0 °C |
2.62 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| 0.700 J/cm² @Temperature 23.0 °C |
3.33 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 239 °C | 462 °F | 80*10*4 s=60mm; ISO 75-1 a |
| Vicat Softening Point | 248 °C | 478 °F | B/120; ISO 306 |
| Flammability, UL94 | V-0 | V-0 | |
| Glow Wire Test | 750 °C @Thickness 1.00 mm |
1380 °F @Thickness 0.0394 in |
GWIT; IEC 60695-2-13 |
| 960 °C @Thickness 2.00 mm |
1760 °F @Thickness 0.0787 in |
GWFI; IEC 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Comparative Tracking Index | >= 600 V | >= 600 V | IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 280 - 295 °C | 536 - 563 °F | |
| Mold Temperature | 70.0 - 90.0 °C | 158 - 194 °F | |
| Drying Temperature | 80.0 °C @Time 7200 - 21600 sec |
176 °F @Time 2.00 - 6.00 hour |
|
| Moisture Content | <= 0.20 % | <= 0.20 % |
Users viewing this material also viewed the following:
- MV Labs SN550 (NH4)2SnF6 Ammonium hexafluorostannate(IV)
- SABIC Innovative Plastics Lexan® AD4820 PC (Europe-Africa-Middle East)
- Michelman® Michem® Lube 180 Anionic co-emulsion of carnauba and paraffin waxes
- IRPC Polimaxx Polene PE100N Polypropylene Wax
- LyondellBasell Petrothene® NA373242 Low Density Polyethylene, Cast/Blown Film Grade
- Samyang Triel® 5350 Thermoplastics Polyetherester Elastomer, General Extrusion
- A. Schulman CP808-01 Natural Linear, Low-Density Polyethylene
- Borealis HF420FB Polypropylene
- Polyplastics Duranex® 7307 Polybutylene Terephthalate (PBT), Super low warpage, GF filled
- Epoxy Technology EPO-TEK® EJ2189 Electrically Conductive Epoxy
Copyright © lookpolymers.com All Rights Reserved