Samyang Trirex® 3025GNH15 Polycarbonate, Reinforced Flame Retardancy, Non-Halogen
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, 20% Glass Filled |
| Manufacturer | Samyang |
| Trade Name | Trirex® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samyang Trirex® 3025GNH15 Polycarbonate, Reinforced Flame Retardancy, Non-Halogen.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PC is characterized by its excellent impact resistance, dimensional stability and excellent thermal resistance.3025GNH15 is a reinforced, flame retardant, non-halogen grade.Applications: LCD Panel Frame (dimensional stability)Information provided by Samyang.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.30 g/cc | 1.30 g/cc | ASTM D792 |
| Water Absorption | 0.12 % | 0.12 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0030 - 0.0050 cm/cm | 0.0030 - 0.0050 in/in | ASTM D955 |
| Melt Flow | 7.0 g/10 min @Load 1.20 kg, Temperature 300 °C |
7.0 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 121 | 121 | ASTM D785 |
| Tensile Strength | 88.3 MPa | 12800 psi | ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 |
| Flexural Yield Strength | 137 MPa | 19900 psi | ASTM D790 |
| Flexural Modulus | 4.41 GPa | 640 ksi | ASTM D790 |
| Izod Impact, Notched | 0.392 J/cm @Thickness 3.17 mm |
0.735 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 33.0 µm/m-°C | 18.3 µin/in-°F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 151 °C | 304 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 146 °C | 295 °F | ASTM D648 |
| Flammability, UL94 | V-2 @Thickness 0.790 mm |
V-2 @Thickness 0.0311 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 4.00e+16 ohm-cm | 4.00e+16 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.11 | 3.11 | ASTM D150 |
| Dielectric Strength | 31.0 kV/mm | 787 kV/in | ASTM D149 |
| Dissipation Factor | 0.0097 | 0.0097 | ASTM D150 |
| Arc Resistance | 120 sec | 120 sec | ASTM D495 |
Users viewing this material also viewed the following:
- Polycasa Acryl® KR 2014/1 Acrylic, Impact Grade
- Resin Technology Group 390 Surface Insensitive Fusion™ Cyanoacrylate Instant Ethyl Adhesive
- PolyOne Elastamax™ EG-9182 Thermoplastic Elastomer (TPE)
- SABIC Innovative Plastics Valox® 7062HP PBT (Europe-Africa-Middle East)
- ExxonMobil Exterex™ P81 Synthetic Fluid
- DuPont™ Fusabond® E589 Polymer Modifier
- ExxonMobil Label-Lyte® 15 LLG-101 Clear OPP Film
- ExxonMobil Gargoyle Arctic C Heavy
- Colorite Polymers 7811 Clear Extrusion Vinyl Compound
Copyright © lookpolymers.com All Rights Reserved