Samyang Tribit® 1500GN30 Polybutylene Terephthalate, 30% Glass Reinforced, Flame Retardant
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), Glass Fiber Filled, Flame Retardant |
| Manufacturer | Samyang |
| Trade Name | Tribit® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samyang Tribit® 1500GN30 Polybutylene Terephthalate, 30% Glass Reinforced, Flame Retardant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Characteristics:G/F reinforcedFlame retardantHeat and Impact resistantApplications:AutomotiveConnectorGearOutdoor handleIgnition systemElectronicConnectorGas valveCoil bobbinSwitch caseRelay caseO/A partsAll information provided by Samyang
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.59 g/cc | 1.59 g/cc | ASTM D792 |
| Water Absorption | 0.070 % @Time 86400 sec |
0.070 % @Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage | 0.0020 - 0.012 cm/cm @Thickness 3.00 mm |
0.0020 - 0.012 in/in @Thickness 0.118 in |
ASTM D955 |
| Melt Flow | 45 g/10 min @Load 5.00 kg, Temperature 250 °C |
45 g/10 min @Load 11.0 lb, Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | ASTM D785 |
| Tensile Strength, Yield | 123 MPa | 17800 psi | ASTM D638 |
| Elongation at Break | 5.0 % | 5.0 % | ASTM D638 |
| Flexural Yield Strength | 172 MPa | 24900 psi | ASTM D790 |
| Flexural Modulus | 8.04 GPa | 1170 ksi | ASTM D790 |
| Izod Impact, Unnotched | 0.883 J/cm @Thickness 3.17 mm |
1.65 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 30.0 µm/m-°C | 16.7 µin/in-°F | ASTM D696 |
| Melting Point | 226 °C | 439 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 225 °C | 437 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 1.59 mm |
V-0 @Thickness 0.0625 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.2 @Frequency 1.00e+6 Hz |
3.2 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Dielectric Strength | 20.0 kV/mm | 508 kV/in | ASTM D149 |
| Dissipation Factor | 0.016 @Frequency 1.00e+6 Hz |
0.016 @Frequency 1.00e+6 Hz |
ASTM D150 |
| Arc Resistance | 110 sec | 110 sec | ASTM D495 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 240 - 260 °C | 464 - 500 °F | |
| Middle Barrel Temperature | 230 - 250 °C | 446 - 482 °F | |
| Front Barrel Temperature | 220 - 230 °C | 428 - 446 °F | |
| Nozzle Temperature | 250 - 270 °C | 482 - 518 °F | |
| Melt Temperature | 265 °C | 509 °F | |
| Drying Temperature | 110 - 130 °C | 230 - 266 °F | |
| Dry Time | 4 - 6 hour | 4 - 6 hour | |
| Moisture Content | 0.010 - 0.015 % | 0.010 - 0.015 % | |
| Screw Speed | 60 - 80 rpm | 60 - 80 rpm |
Users viewing this material also viewed the following:
- S&E Specialty Polymers GPP1001V0M-HCO-15 PP
- Kinlead LSD11 Low Temperature Grade Heat Sealable Film (thickness: 20 µm)
- LATI Latilon 28D PC
- LyondellBasell Hostacomâ„¢ CB267 Thermoplastic Polyolefin Elastomer
- A. Schulman POLYFORT™ FPP 1607 Talc Filled Homopolymer Polypropylene
- A. Schulman CP763-01 Extruded, Blow Molding and Injection Molding Grade Polyethylene
- Axiall 02541 Plenum Flexible PVC
- Bulk Molding Compounds BMC 6241 Glass Reinforced BMC
- Plenco 6554 Phenolic, Granular, Compression Molded (discontinued **)
- Materion ToughMet® T3 AT90 (OD
Copyright © lookpolymers.com All Rights Reserved