Samsung Cheil Industries Starex® WX-9700 ASA, Unreinforced Extrusion Grade
| Category | Polymer , Thermoplastic , ASA Polymer , Acrylonitrile/Styrene/Acrylate (ASA), Unreinforced, Molded |
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | Starex® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Starex® WX-9700 ASA, Unreinforced Extrusion Grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Samsung Cheil Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.07 g/cc | 1.07 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0070 - 0.0090 cm/cm @Thickness 3.20 mm |
0.0070 - 0.0090 in/in @Thickness 0.126 in |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0078 cm/cm @Thickness 3.20 mm |
0.0078 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 9.0 g/10 min @Load 10.0 kg, Temperature 220 °C |
9.0 g/10 min @Load 22.0 lb, Temperature 428 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 99 | 99 | ASTM D785 |
| Tensile Strength at Break | 40.2 MPa | 5830 psi | 5 mm/min; ASTM D638 |
| Tensile Strength, Yield | 42.2 MPa | 6120 psi | 5 mm/min; ASTM D638 |
| Elongation at Break | 75 % | 75 % | 5 mm/min; ASTM D638 |
| Tensile Modulus | 1.92 GPa | 279 ksi | 5 mm/min; ASTM D638 |
| Flexural Strength | 60.8 MPa | 8820 psi | 2.8 mm/min; ASTM D638 |
| Flexural Modulus | 1.96 GPa | 284 ksi | 2.8 mm/min; ASTM D638 |
| Izod Impact, Notched | 0.981 J/cm @Thickness 6.35 mm |
1.84 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| 4.90 J/cm @Thickness 3.17 mm |
9.18 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 77.0 °C @Thickness 6.40 mm |
171 °F @Thickness 0.252 in |
ASTM D648 |
| Vicat Softening Point | 96.0 °C | 205 °F | B/50; ISO R306 |
Users viewing this material also viewed the following:
- Ineos ABS Lustran® H702
- Kuraray SEPTON® S8006 Thermoplastic Rubber
- Solvay Specialty Polymers Aquivion® E98-09S Tetrafluoroethylene + SFVE (TFE+SFVE)
- SPS Guang Zhou REMAKâ„¢ 7001RM4 Flame-retarded PS masterbatch
- Suqian Unitechem Antioxidant 1076
- DSM Arnitel® PL581 58 Shore D, Injection Grade Copolyester Elastomer (North America)
- DuPont Performance Polymers Zytel® 8018HS BKB085 Nylon 66 (Unverified Data**)
- DuPont Teijin Films Mylar® LJP Polyester Film, 275 Gauge
- DuPont Teijin Films Mylar® OWF Polyester Film, 48 Gauge
- 3M AC-236 Class A-1/2 Aerospace Sealant
Copyright © lookpolymers.com All Rights Reserved