Samsung Cheil Industries Starex® VE-0852 ABS, Unreinforced FR

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Unreinforced, Flame Retardant
Manufacturer Samsung, Cheil Industries
Trade Name Starex®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Samsung Cheil Industries Starex® VE-0852 ABS, Unreinforced FR.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by Samsung Cheil Industries.
Physical Properties Metric English Comments
Specific Gravity 1.20 g/cc
1.20 g/cc
ASTM D792
Linear Mold Shrinkage, Flow 0.0030 - 0.0060 cm/cm

@Thickness 3.20 mm
 0.0030 - 0.0060 in/in

@Thickness 0.126 in
 ASTM D955
Melt Flow 1.6 g/10 min

@Load 5.00 kg,
Temperature 200 °C
 1.6 g/10 min

@Load 11.0 lb,
Temperature 392 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 79
79
ASTM D785
Tensile Strength at Break 28.4 MPa
4120 psi
5 mm/min; ASTM D638
Tensile Strength, Yield 33.3 MPa
4840 psi
5 mm/min; ASTM D638
Elongation at Break 56 %
56 %
5 mm/min; ASTM D638
Tensile Modulus 1.47 GPa
213 ksi
5 mm/min; ASTM D638
Flexural Strength 48.1 MPa
6980 psi
2.8 mm/min; ASTM D638
Flexural Modulus 1.57 GPa
228 ksi
2.8 mm/min; ASTM D638
Izod Impact, Notched 2.84 J/cm

@Thickness 6.35 mm
 5.33 ft-lb/in

@Thickness 0.250 in
 ASTM D256
4.41 J/cm

@Thickness 3.17 mm
 8.27 ft-lb/in

@Thickness 0.125 in
 ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 93.0 °C

@Thickness 6.40 mm
 199 °F

@Thickness 0.252 in
 ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 83.0 °C

@Thickness 6.40 mm
 181 °F

@Thickness 0.252 in
 ASTM D648
Vicat Softening Point 87.0 °C
189 °F
B/50; ISO R306
91.0 °C
196 °F
B/120; ISO R306