- Honeywell Capran® Oxyshield™ M-OPA (0.60 mil) Monoaxially Oriented, Co-Extruded In-Line Nylon6/Nylon6/Nylon6 Film
Honeywell Capran® Oxyshield™ M-OPA (0.60 mil) Monoaxially Oriented, Co-Extruded In-Line Nylon6/Nylon6/Nylon6 Film
| Category | Polymer , Film , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Film Grade |
| Manufacturer | Honeywell |
| Trade Name | Capran® Oxyshield™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Honeywell Capran® Oxyshield™ M-OPA (0.60 mil) Monoaxially Oriented, Co-Extruded In-Line Nylon6/Nylon6/Nylon6 Film.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Capran® Oxyshield™ M-OPA (Machine Direction Oriented Polyamide) is a clear, monoaxially oriented, co-extruded in-line nylon6/nylon6/nylon6 film with high mechanical strength and good gas barrier properties for packaging. Information provided by Honeywell.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc | 0.0410 lb/in³ | Yield Density |
| Oxygen Transmission Rate | 37.0 - 43.0 cc/m²/day | 2.38 - 2.77 cc/100 in²/day | 73°F (23°C) / 65%RH; ASTM D3985 |
| Thickness | 15.2 microns | 0.600 mil | |
| Surface Tension | >= 56 dynes/cm | >= 56 dynes/cm | treated side; ASTM D2578 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Tensile Strength at Yield, TD | 59.3 - 75.8 MPa | 8600 - 11000 psi | ASTM D882 |
| Film Elongation at Break, MD | 65 - 95 % | 65 - 95 % | ASTM D882 |
| Film Elongation at Break, TD | 300 - 425 % | 300 - 425 % | ASTM D882 |
| Secant Modulus, MD | 1.724 - 2.586 GPa | 250.0 - 375.1 ksi | ASTM D882 |
| Secant Modulus, TD | 1.896 - 2.758 GPa | 275.0 - 400.0 ksi | ASTM D882 |
| Coefficient of Friction | 0.16 - 0.30 | 0.16 - 0.30 | film to stainless steel; ASTM D1894 |
| 0.60 - 1.0 | 0.60 - 1.0 | film to film; ASTM D1894 | |
| Tear Strength Test | 1100 - 1500 | 1100 - 1500 | graves tear MD, grams/mil; ASTM D1004 |
| 1100 - 1500 | 1100 - 1500 | graves tear TD, grams/mil; ASTM D1004 | |
| Film Tensile Strength at Break, MD | 290 - 372 MPa | 42000 - 54000 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 68.9 - 96.5 MPa | 10000 - 14000 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Shrinkage, MD | <= 10 % | <= 10 % | 350°F / 177°C - 10 min.; ASTM D1204 |
| Shrinkage, TD | <= 1.5 % | <= 1.5 % | 350°F / 177°C - 10 min.; ASTM D1204 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | <= 5.5 % | <= 5.5 % | ASTM D1003 |
Users viewing this material also viewed the following:
- Materion Beryllium Copper Alloy 3 Plate & Rolled Bar; AT (TF00) Temper; All Thicknesses (UNS C17510)
- Kostat 7440 Conductive ABS Compound
- Lanxess Durethan® BKV 130 H3.0 DUS008 000000 Nylon 6, 30% Glass Fiber
- LATI Latan 13 G/30 POM, 30% Glass Fiber Reinforced
- Special Metals INCONEL® 725 Nickel Superalloy (UNS N07725), Annealed Tube
- Shakespeare LMX-3 Easy Casting Nylon Copolymer Fishing Line, 30 lb
- Formosa Plastics 50% Liquid Caustic Soda Membrane Grade
- Dow DOWLEX™ 2500 Linear Low Density Polyethylene, Narrow MW Distribution
- ChevronTexaco ISO 100 Industrial Oil EP
Copyright © lookpolymers.com All Rights Reserved