SABIC Innovative Plastics Cycolac® INP222 ABS
| Category | Polymer , Thermoplastic , ABS Polymer |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Cycolac® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Cycolac® INP222 ABS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Bulk MMASAN. Provides an economical option for achieving greater melt strength in polymers.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.12 g/cc | 1.12 g/cc | ASTM D792 |
| Density | 1.12 g/cc | 0.0405 lb/in³ | ISO 1183 |
| Melt Flow | 18.3 g/10 min @Load 3.80 kg, Temperature 230 °C |
18.3 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM D1238 |
| 48 g/10 min @Load 10.0 kg, Temperature 220 °C |
48 g/10 min @Load 22.0 lb, Temperature 428 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 121 | 121 | ASTM D785 |
| Flexural Yield Strength | 92.0 MPa | 13300 psi | 2 mm/min; ISO 178 |
| 114 MPa | 16500 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 2.90 GPa | 421 ksi | 2 mm/min; ISO 178 |
| 3.52 GPa | 511 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.240 J/cm | 0.450 ft-lb/in | ASTM D256 |
| 0.150 J/cm @Temperature -30.0 °C |
0.281 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| Izod Impact, Notched (ISO) | 2.00 kJ/m² | 0.952 ft-lb/in² | 80*10*4; ISO 180/1A |
| 1.00 kJ/m² @Temperature -30.0 °C |
0.476 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Charpy Impact, Notched | 0.100 J/cm² | 0.476 ft-lb/in² | ISO 179/2C |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 86.0 °C @Thickness 3.20 mm |
187 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 75.0 °C | 167 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 75.0 °C @Thickness 3.20 mm |
167 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 93.0 °C | 199 °F | Rate B/50; ISO 306 |
| 95.0 °C | 203 °F | Rate B/120; ISO 306 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Yellow Index | 1.0 % | 1.0 % | ASTM D1925 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics LNP KONDUIT PTF2BXXX PA 6 (Europe-Africa-Middle East)
- Special Metals INCONEL® 706 Precipitation Hardening Alloy, Hot Finished Flat, 2 Part Heat Treatment, 1.250 inch (31.8 mm) Thickness
- Unifrax Fiberfrax® Topcoat™ 2600 Insulating Mix
- Zircar Zirconia ZYF-150 Zirconia Felt Insulation
- Cossa Polimeri ESTALUX 9206 A Methyl Methacrylate Acrylonitrile Butadiene Styrene
- Bapolan® ABS8430 ABS Polymer, Extrusion/Injection Grade
- 3M 200 Paper Tape
- PolyOne Synprene® RT-3640 Thermoplastic Elastomer - SBC (discontinued **)
- BASF Ultramid® N-265 NF3001 40% Mineral Filled PA66 (Dry)
Copyright © lookpolymers.com All Rights Reserved