- Samsung Cheil Industries Starex® SR-0315 ABS, Unreinforced Heat Resistant
Samsung Cheil Industries Starex® SR-0315 ABS, Unreinforced Heat Resistant
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Heat Resistant, Molded |
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | Starex® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Starex® SR-0315 ABS, Unreinforced Heat Resistant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Samsung Cheil Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.04 g/cc | 1.04 g/cc | ASTM D792 |
| Water Absorption | 0.050 % @Temperature 23.0 °C |
0.050 % @Temperature 73.4 °F |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0060 cm/cm @Thickness 3.20 mm |
0.0060 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 10 g/10 min @Load 10.0 kg, Temperature 220 °C |
10 g/10 min @Load 22.0 lb, Temperature 428 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 109 | 109 | ASTM D785 |
| Tensile Strength, Yield | 43.1 MPa | 6260 psi | 5 mm/min; ASTM D638 |
| Elongation at Break | 14 % | 14 % | 5 mm/min; ASTM D638 |
| Flexural Strength | 61.8 MPa | 8960 psi | 2.8 mm/min; ASTM D790 |
| Flexural Modulus | 2.06 GPa | 299 ksi | 2.8 mm/min; ASTM D790 |
| Izod Impact, Notched | 1.67 J/cm @Thickness 6.35 mm |
3.12 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| 1.77 J/cm @Thickness 3.17 mm |
3.31 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 86.0 °C @Thickness 6.40 mm |
187 °F @Thickness 0.252 in |
ASTM D648 |
| Vicat Softening Point | 103 °C | 217 °F | B/50; ISO R306 |
Users viewing this material also viewed the following:
- Polimeri Europa Eraclene® MM 74 High Density Polyethylene - Injection Molding
- Guarniflon PTFE G427 Polytetrafluoroethylene 40% Bronze, 5% Molybdenum Disulfide
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 1-D Heavy Oil Plasticizer
- Eurostar Starflam PX06011 PA6, Glass Fiber Filled, Flame Retardant, Injection Molded
- Braskem LF320 LLDPE Cast Film Extrusion Polyethylene Copolymer
- BorsodChem ONGROVIL S-468 Suspension PVC-Resin
- Lord Adhesives 201 Semi-Flexible, Medium Cure, Medium Viscosity Acrylic Adhesive
- Phillips Sumika Marlex® ABF-035 Thermoplastic Polyolefin (discontinued **)
Copyright © lookpolymers.com All Rights Reserved