- Samsung Cheil Industries Infino® WP-1041 PC/ABS, Unreinforced Metal Plating Grade
Samsung Cheil Industries Infino® WP-1041 PC/ABS, Unreinforced Metal Plating Grade
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) |
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | Infino® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Infino® WP-1041 PC/ABS, Unreinforced Metal Plating Grade.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
High flow PC/ABS material that can be used for automobile R/G door handleInformation provided by Samsung Cheil Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.09 g/cc | 1.09 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0060 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0060 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 4.0 g/10 min @Load 2.16 kg, Temperature 250 °C |
4.0 g/10 min @Load 4.76 lb, Temperature 482 °F |
ASTM D1238 |
| 35 g/10 min @Load 10.0 kg, Temperature 250 °C |
35 g/10 min @Load 22.0 lb, Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 103 | 103 | ASTM D785 |
| Tensile Strength, Yield | 48.1 MPa | 6970 psi | 50 mm/min; ASTM D638 |
| Elongation at Break | 25 % | 25 % | 50 mm/min; ASTM D638 |
| Flexural Strength | 65.7 MPa | 9530 psi | 2.8 mm/min; ASTM D638 |
| Flexural Modulus | 1.86 GPa | 270 ksi | 2.8 mm/min; ASTM D638 |
| Izod Impact, Notched | 3.92 J/cm @Thickness 6.35 mm |
7.35 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| 5.39 J/cm @Thickness 3.17 mm |
10.1 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 99.0 °C @Thickness 6.40 mm |
210 °F @Thickness 0.252 in |
ASTM D648 |
| Vicat Softening Point | 110 °C | 230 °F | B/50; ISO R306 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics LNP KONDUIT OX11314 PPS (Asia Pacific)
- Ensinger ENSITEP® PET Polyethylene Terephthalate - Extruded Products (discontinued **)
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber, 0.20 PHR Caytur 4
- Lubriplate 730-1 Aluminum Complex Multi-Purpose Grease
- H.C. Starck Baymetec® Tantalum Silicide, Ta5Si3
- SABIC Innovative Plastics LNP STAT-KON DD000 PC (Asia Pacific)
- Clariant Renol PA111G60 Nylon 66, 60% Glass Fiber
- Materion Beryllium Copper Alloy 3 Wire; AT (TF00) Temper; 1.3-12.7 mm Diameter (UNS C17510)
- Johnson Matthey JM P40 Soft Solder/Flux
Copyright © lookpolymers.com All Rights Reserved