- Samsung Cheil Industries Infino® VB-5300G PBT, Glass Filled FR
Samsung Cheil Industries Infino® VB-5300G PBT, Glass Filled FR
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), Glass Fiber Filled, Flame Retardant |
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | Infino® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Infino® VB-5300G PBT, Glass Filled FR.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Samsung Cheil Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.63 g/cc | 1.63 g/cc | ASTM D792 |
| Water Absorption | 0.060 % @Temperature 23.0 °C |
0.060 % @Temperature 73.4 °F |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0090 cm/cm @Thickness 3.20 mm |
0.0030 - 0.0090 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 15 g/10 min @Load 2.16 kg, Temperature 250 °C |
15 g/10 min @Load 4.76 lb, Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | ASTM D785 |
| Tensile Strength, Yield | 127 MPa | 18500 psi | 5 mm/min; ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | 5 mm/min; ASTM D638 |
| Flexural Strength | 186 MPa | 27000 psi | 2.8 mm/min; ASTM D638 |
| Flexural Modulus | 8.83 GPa | 1280 ksi | 2.8 mm/min; ASTM D638 |
| Izod Impact, Notched | 0.735 J/cm @Thickness 3.17 mm |
1.38 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C @Thickness 6.40 mm |
410 °F @Thickness 0.252 in |
ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 0.750 - 3.00 mm |
V-0 @Thickness 0.0295 - 0.118 in |
Users viewing this material also viewed the following:
- Lanxess Durethan® C 38 FKAM 000000 Copolyamide
- Teknor Apex APEX® 3611-80 Polyvinyl Chloride, Flexible
- Solvay MIRACARE® PLAISANT Surfactant
- Cosmic Plastics 6220F Short Glass Fiber Filled Iso Diallyl Phthalate Molding Compound
- A. Schulman SCHULAMID® 66 GB40 40% Glass Bead Reinforced Nylon 66
- TSE Industries Millathane® E34 Millable Polyether Polyurethane Rubber with TP-95
- Ensinger TECAPRO™ SAN Polypropylene (PP)
- Dow AFFINITY™ PT 1450G1 Ethylene alpha-olefin resin
- Dow Latex LXC 811NA Carboxylated Styrene-Butadiene Latex
- Shinkong Synthetic Fibers Shinite® C501G15 Nylon 6, 15% Glass Filled
Copyright © lookpolymers.com All Rights Reserved