Samsung Cheil Industries Infino® VB-3100G PBT/ABS, Glass Filled FR
| Category | Polymer , Thermoplastic , ABS Polymer , ABS/Polyester Alloy + GF , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | Infino® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Infino® VB-3100G PBT/ABS, Glass Filled FR.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Samsung Cheil Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.45 g/cc | 1.45 g/cc | ASTM D792 |
| Water Absorption | 0.080 % @Temperature 23.0 °C |
0.080 % @Temperature 73.4 °F |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0070 - 0.011 cm/cm @Thickness 3.20 mm |
0.0070 - 0.011 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 30 g/10 min @Load 2.16 kg, Temperature 250 °C |
30 g/10 min @Load 4.76 lb, Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 113 | 113 | ASTM D785 |
| Tensile Strength, Yield | 73.5 MPa | 10700 psi | 5 mm/min; ASTM D638 |
| Elongation at Break | 4.0 % | 4.0 % | 5 mm/min; ASTM D638 |
| Flexural Strength | 108 MPa | 15700 psi | 2.8 mm/min; ASTM D638 |
| Flexural Modulus | 4.22 GPa | 612 ksi | 2.8 mm/min; ASTM D638 |
| Izod Impact, Notched | 0.490 J/cm @Thickness 3.17 mm |
0.918 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 150 °C @Thickness 6.40 mm |
302 °F @Thickness 0.252 in |
ASTM D648 |
| Vicat Softening Point | 147 °C | 297 °F | B/50; ISO R306 |
| Flammability, UL94 | V-0 @Thickness 1.50 - 3.00 mm |
V-0 @Thickness 0.0591 - 0.118 in |
Users viewing this material also viewed the following:
- Resin Technology Group 405 Oxy-Bond™ Electrically Conductive Epoxy Adhesive
- Covestro Apec® DP9-9341 High-Heat Polycarbonate, General Purpose (discontinued **)
- Garlock 3205 Neoprene/Polyester Fabric
- Lucent Polymers CPP-120 Polypropylene Homopolymer, 20% Calcium Carbonate Filled
- Solvay Chemicals E9000 Chloroform
- Solvay Specialty Polymers EpiSpire® EP-340 Sulfone, High Temperature (HTS)
- Formosa Plastics 50% Liquid Caustic Soda Membrane Grade
- Eagle Brass 430 Ferritic Stainless Steel, Full Hardened
- Fainplast Compounds GS 8202 Flexible PVC, Injection Molding for Footwear
Copyright © lookpolymers.com All Rights Reserved