Samsung Cheil Industries Infino® PCA-NH1015V Flame Retardant
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) |
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | Infino® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Infino® PCA-NH1015V Flame Retardant.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.17 g/cc | 0.0423 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 30 g/10 min @Load 10.0 kg, Temperature 220 °C |
30 g/10 min @Load 22.0 lb, Temperature 428 °F |
ASTM 1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 118 | 118 | ASTM D785 |
| Tensile Strength, Ultimate | 48.0 MPa | 6960 psi | ASTM D638 |
| Tensile Modulus | 2.50 GPa | 363 ksi | ISO 527-2/50 |
| Flexural Strength | 84.8 MPa | 12300 psi | ASTM D790 |
| Flexural Modulus | 2.40 GPa | 348 ksi | ASTM D790 |
| Izod Impact, Notched | 5.34 J/cm | 10.0 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 94.0 °C | 201 °F | Unannealed; ISO 75-2/B |
| Deflection Temperature at 1.8 MPa (264 psi) | 86.0 °C @Thickness 6.35 mm |
187 °F @Thickness 0.250 in |
Unannealed; ASTM D648 |
| Vicat Softening Point | 100 - 102 °C | 212 - 216 °F | ISO 306, B50 |
| Flammability, UL94 | V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
|
| 5VB @Thickness 2.00 mm |
5VB @Thickness 0.0787 in |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Flexible 90039 Polyvinyl Chloride, Flexible (PVC, Flexible)
- PolyOne Edgetek® AS-50GF/000 Acrylonitrile Butadiene Styrene (ABS), Glass Filled (discontinued **)
- SABIC Innovative Plastics LNP LUBRICOMP 5CL23 FP-V (PVDF)
- SABIC Innovative Plastics NORYL V090 PPE+HIPS (Europe-Africa-Middle East)
- A. Schulman POLYBATCH™ Poly Off-White P90062PF Concentrate Based In Polypropylene
- Covestro Bayblend® T88 GF-10* Polycarbonate + SAN Glass Filled Impact Grade
- CIP Composites 200 Series Laminated Polymer Bearing Material
- Braskem TI2350C High Crystallinity Copolymer Polypropylene
- BASF Elastollan® C-60D Polyester Type Polyurethane Elastomer
- Bhansali Engineering Santron IMS1000M SAN Resin
Copyright © lookpolymers.com All Rights Reserved