SABIC Innovative Plastics Xylex X7509UV PC+POLYESTER (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polyester, TP
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Xylex
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics Xylex X7509UV PC+POLYESTER (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
PC+POLYESTER, Transparent, UV-Stabilized,This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
Physical Properties Metric English Comments
Specific Gravity 1.20 g/cc
1.20 g/cc
ASTM D 792
Density 1.20 g/cc
0.0434 lb/in³
ISO 1183
Linear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm

@Thickness 3.20 mm
 0.0050 - 0.0070 in/in

@Thickness 0.126 in
 SABIC Method
Melt Flow 12 g/10 min

@Load 2.16 kg,
Temperature 265 °C
 12 g/10 min

@Load 4.76 lb,
Temperature 509 °F
 ASTM D 1238
12 g/10 min

@Load 2.16 kg,
Temperature 265 °C
 12 g/10 min

@Load 4.76 lb,
Temperature 509 °F
 [cm^3/10 min] Melt Volume Rate; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 62.0 MPa
8990 psi
50 mm/min; ISO 527
64.0 MPa
9280 psi
Type I, 50 mm/min; ASTM D 638
Tensile Strength, Yield 60.0 MPa
8700 psi
50 mm/min; ISO 527
61.0 MPa
8850 psi
Type I, 50 mm/min; ASTM D 638
Elongation at Break 133 %
133 %
50 mm/min; ISO 527
135 %
135 %
Type I, 50 mm/min; ASTM D 638
Elongation at Yield 5.8 %
5.8 %
50 mm/min; ISO 527
6.3 %
6.3 %
Type I, 50 mm/min; ASTM D 638
Tensile Modulus 2.30 GPa
334 ksi
1 mm/min; ISO 527
Flexural Yield Strength 92.0 MPa
13300 psi
2 mm/min; ISO 178
96.0 MPa
13900 psi
1.3 mm/min, 50 mm span; ASTM D 790
Flexural Modulus 2.25 GPa
326 ksi
2 mm/min; ISO 178
2.34 GPa
339 ksi
1.3 mm/min, 50 mm span; ASTM D 790
Izod Impact, Notched 7.13 J/cm

@Temperature 23.0 °C
 13.4 ft-lb/in

@Temperature 73.4 °F
 ASTM D 256
Izod Impact, Notched (ISO) 6.00 kJ/m²

@Temperature -30.0 °C
 2.86 ft-lb/in²

@Temperature -22.0 °F
 80*10*4; ISO 180/1A
9.00 kJ/m²

@Temperature 23.0 °C
 4.28 ft-lb/in²

@Temperature 73.4 °F
 80*10*4; ISO 180/1A
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 90.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 50.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
104 µm/m-°C

@Temperature -40.0 - 40.0 °C
 57.8 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
CTE, linear, Transverse to Flow 90.0 µm/m-°C

@Temperature -40.0 - 40.0 °C
 50.0 µin/in-°F

@Temperature -40.0 - 104 °F
 ISO 11359-2
100 µm/m-°C

@Temperature -40.0 - 40.0 °C
 55.6 µin/in-°F

@Temperature -40.0 - 104 °F
 ASTM E 831
Deflection Temperature at 1.8 MPa (264 psi) 106 °C
223 °F
Flatw 80*10*4 sp=64mm; ISO 75/Af
106 °C

@Thickness 3.20 mm
 223 °F

@Thickness 0.126 in
 unannealed; ASTM D 648
Vicat Softening Point 126 °C
259 °F
Rate B/50; ASTM D 1525
126 °C
259 °F
Rate B/50; ISO 306
126 °C
259 °F
Rate B/120; ISO 306
Optical Properties Metric English Comments
Haze <= 2.0 %

@Thickness 2.54 mm
 <= 2.0 %

@Thickness 0.100 in
 ASTM D 1003
Transmission, Visible 89 %

@Thickness 2.54 mm
 89 %

@Thickness 0.100 in
 ASTM D 1003