Samsung Cheil Industries Starex® SG-302 Expandable Polystyrene (EPS) High Expansion
| Category | Polymer , Thermoplastic , Polystyrene (PS) , Expanded Polystyrene (EPS) |
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | Starex® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Starex® SG-302 Expandable Polystyrene (EPS) High Expansion.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Typical Application : Large Float, Fish Box (Large)Information provided by Samsung Cheil Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.03 - 1.05 g/cc | 1.03 - 1.05 g/cc | |
| Density | 0.0160 g/cc | 0.000578 lb/in³ | Based on 65 times expansion |
| Bead Size | 0.720 - 0.960 mm | 0.0283 - 0.0378 in | JIS Z8801 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Flexural Strength | 2.40 MPa | 348 psi | @ 20 kg/m<sup>2</sup>; ASTM DC201 |
| Compressive Strength | >= 1.10 MPa | >= 160 psi | @ 20 kg/m<sup>2</sup>; JIS A9511, ASTM D1621 |
| Chemical Properties | Metric | English | Comments |
|---|---|---|---|
| Blowing Agent Content | 6.0 - 7.0 % | 6.0 - 7.0 % | Pentane |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Blocking | <1% | |
| Expandability | 65 Times | Expansion for 5 min Cheil Method |
| Fusion | >65% | Cheil Method |
| Polymer Content | 93-94% |
Users viewing this material also viewed the following:
- Oceanchem Group Ammonium Bromide Photo Grade I
- SABIC Innovative Plastics LNP LUBRICOMP DFP34 PC (Europe-Africa-Middle East)
- Polycasa Acryl® KR 2008/1 Acrylic, Impact Grade
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 30 PHR Suprex Clay Filler
- Lucent Polymers CPP-220 Polypropylene, 20% Calcium Carbonate Filled, Impact Modified
- SK Chemicals SKYTHANE® UB400 Hotmelt Lamination Film
- EMS-Grivory Grivory® AS V0 PA66
- Dow Nordel® IP 4725P Heat Resistant Molding
- Ascend Performance Materials Vydyne® R530H NAT Nylon 66, 30% Glass Reinforced, Conditioned
Copyright © lookpolymers.com All Rights Reserved