PolyOne Elastamax XL 0233-1 Polyurethane Compound (discontinued **)

Category	Polymer , Thermoplastic , Polyurethane, TP
Manufacturer
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	PolyOne Elastamax XL 0233-1 Polyurethane Compound (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

This is a static dissipative thermoplastic polyurethane compound for injection molding and extrusion applications. Physical Form: Pellet. Standard Color: Black/grey.Information provided by M. A. Hanna. M. A. Hanna and Geon merged to form PolyOne in 2000.

Physical Properties	Metric	English	Comments
Density	1.18 g/cc	0.0426 lb/in³	ASTM D792
Melt Flow	14.8 g/10 min @Load 2.16 kg, Temperature 230 °C	14.8 g/10 min @Load 4.76 lb, Temperature 446 °F	ASTM D1238
	40 g/10 min @Load 5.00 kg, Temperature 230 °C	40 g/10 min @Load 11.0 lb, Temperature 446 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	20.4 MPa	2960 psi	10 in/min; ASTM D412
Elongation at Break	60 %	60 %	10 in/min; ASTM D412
50% Modulus	0.01903 GPa	2.760 ksi	10 in/min; ASTM D412
Tear Strength	102 kN/m	580 pli	Die 'C' Tear; 20 in/min; ASTM D624
Compression Set	45 % @Temperature 70.0 °C	45 % @Temperature 158 °F	22 hrs; ASTM D395

Electrical Properties	Metric	English	Comments
Electrical Resistivity	2.70e+8 ohm-cm	2.70e+8 ohm-cm	ASTM D257
Surface Resistance	1.30e+8 ohm	1.30e+8 ohm	ASTM D257