SABIC Innovative Plastics Valox® IQ507 PBT+PC (Asia Pacific)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/Polybutylene Terephthalate (PBT) Blend, Glass Filled , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Valox® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Valox® IQ507 PBT+PC (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Valox iQ507 resin: Environmentally responsible, sustainable, and low carbon footprint resin that is 30% glass fiber reinforced PBT+PC alloy. Valox iQ507 offers good mechanical and thermal characteristics, along with reduced warpage characteristics.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.51 g/cc | 1.51 g/cc | ASTM D792 |
| Density | 1.51 g/cc | 0.0546 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.0800 % | 0.0800 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.10 % | 0.10 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0040 cm/cm @Thickness 3.20 mm |
0.0010 - 0.0040 in/in @Thickness 0.126 in |
SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0040 - 0.0080 cm/cm @Thickness 3.20 mm |
0.0040 - 0.0080 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 50 g/10 min @Load 5.00 kg, Temperature 250 °C |
50 g/10 min @Load 11.0 lb, Temperature 482 °F |
ASTM D1238 |
| Melt Index of Compound | 38 g/10 min @Load 5.00 kg, Temperature 250 °C |
38 g/10 min @Load 11.0 lb, Temperature 482 °F |
MVR [cm^3/10 min]; ISO 1133 |
| 43 g/10 min @Load 5.00 kg, Temperature 220 °C |
43 g/10 min @Load 11.0 lb, Temperature 428 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 119 | 119 | ASTM D785 |
| Tensile Strength at Break | 96.0 MPa | 13900 psi | 5 mm/min; ISO 527 |
| 105 MPa | 15200 psi | Type I, 5 mm/min; ASTM D638 | |
| 132 MPa | 19100 psi | Type I, 10 mm/min; SABIC - Japan Method | |
| Tensile Strength, Yield | 96.0 MPa | 13900 psi | 5 mm/min; ISO 527 |
| 105 MPa | 15200 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 1.0 % | 1.0 % | 5 mm/min; ISO 527 |
| 1.0 % | 1.0 % | Type I, 5 mm/min; ASTM D638 | |
| 7.0 % | 7.0 % | Type I, 10 mm/min; SABIC - Japan Method | |
| Elongation at Yield | 1.0 % | 1.0 % | Type I, 5 mm/min; ASTM D638 |
| 1.0 % | 1.0 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 10.2 GPa | 1480 ksi | 1 mm/min; ISO 527 |
| 12.8 GPa | 1860 ksi | 5 mm/min; ASTM D638 | |
| Flexural Yield Strength | 187 MPa | 27100 psi | 2 mm/min; ISO 178 |
| 196 MPa | 28400 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 8.91 GPa | 1290 ksi | 2 mm/min; ISO 178 |
| 9.06 GPa | 1310 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.840 J/cm | 1.57 ft-lb/in | ASTM D256 |
| 0.700 J/cm @Temperature -30.0 °C |
1.31 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| Izod Impact, Unnotched | 5.93 J/cm | 11.1 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 8.00 kJ/m² | 3.81 ft-lb/in² | 80*10*4; ISO 180/1A |
| 7.00 kJ/m² @Temperature -30.0 °C |
3.33 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Charpy Impact, Notched | 2.10 J/cm² | 9.99 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Dart Drop, Total Energy | 7.00 J @Temperature 23.0 °C |
5.16 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 21.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
11.7 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 21.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
11.7 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| CTE, linear, Transverse to Flow | 81.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
45.0 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| 81.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
45.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 212 °C | 414 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| Deflection Temperature at 1.8 MPa (264 psi) | 186 °C | 367 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 182 °C @Thickness 3.20 mm |
360 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 190 °C | 374 °F | Rate B/120; ISO 306 |
| 192 °C | 378 °F | Rate B/50; ISO 306 | |
| 192 °C | 378 °F | Rate B/50; ASTM D1525 |
Users viewing this material also viewed the following:
- Plastcom SLOVAMID 66 C 15 MI PA66, 15% mineral filling
- Nitriflex NitriClean N-689 B NBR - Nitrile Rubber
- SABIC Innovative Plastics NORYL IGN5531 PPE+PS (Europe-Africa-Middle East)
- ExxonMobil 26 Mobil DTE 20 Series
- A. Schulman POLYBATCH™ Red 502 Concentrate Based In Polyethylene
- EMS-Grivory Grivory® GV-2H black PA*-GF20
- Arlon 51991A020 0.020" (0.508 mm) Uncured Silicone Rubber with Fiberglass Substrate
- PolyOne Synprene® RT-3630 Thermoplastic Elastomer - SBC (discontinued **)
- Eurotec® Tecomid® NB40 NL FY50 PA6, unfilled, flame retardant - halogen & red phosphorus free, natural
- PolyOne Gravi-Tech™ GRV-TP-050-CU-NAT Styrene Butadiene Block Copolymer (SBC)
Copyright © lookpolymers.com All Rights Reserved