Polykemi AB POLYlux 3809S F20 UV2 PC/PBT-Blend, Glass Fiber-Reinforced
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate/Polybutylene Terephthalate (PBT) Blend, Glass Filled , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | Polykemi AB |
| Trade Name | POLYlux |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Polykemi AB POLYlux 3809S F20 UV2 PC/PBT-Blend, Glass Fiber-Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Polykemi AB
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.34 g/cc | 0.0484 lb/in³ | ISO 1183 |
| Filler Content | 20 % | 20 % | ±2%; Polykemi |
| Linear Mold Shrinkage | 0.0040 cm/cm | 0.0040 in/in | With Flow; ISO 2577 |
| 0.0080 cm/cm | 0.0080 in/in | Across Flow; ISO 2577 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | <= 80.0 MPa | <= 11600 psi | ISO/R527 |
| Elongation at Break | 4.0 % | 4.0 % | ISO/R527 |
| Flexural Modulus | 4.80 GPa @Temperature 23.0 °C |
696 ksi @Temperature 73.4 °F |
ISO 178 |
| Charpy Impact, Notched | 1.10 J/cm² @Temperature 23.0 °C |
5.23 ft-lb/in² @Temperature 73.4 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 110 °C | 230 °F | 120°C/h; ISO 75/1 |
| Deflection Temperature at 1.8 MPa (264 psi) | 100 °C | 212 °F | 120°C/h; ISO 75/1 |
| Vicat Softening Point | 125 °C @Load 5.001 kg |
257 °F @Load 11.03 lb |
50°C/h; ISO 306 |
Users viewing this material also viewed the following:
- Nye Lubricants UniFlor 8623G (UF) Synthetic Oil
- SABIC Innovative Plastics Lexan® 503 PC (Asia Pacific)
- RedEye On Demand PolyJet™ Resin, Black, Rapid Prototyping Material
- LATI LAPEX A G/20 20% Glass Fiber Reinforced Polyethersulfone (PES) (UL94 V-0) (Unverified Data**)
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 30 PHR Atomite Whiting Filler
- DuPont Performance Polymers Rynite® 530 BK503 Polyethylene Terephthalate (PET) (Unverified Data**)
- Chosun Refractories HSC-15G Dense and High-Strength Castable, Credens
- Bohler-Uddeholm UDDEHOLM ALVAR 14 Hot Work Tool Steel
- AK Steel 321 Austenitic Stainless steel
- 3M Scotchcast™ 2130 Flame-Retardant Compound
Copyright © lookpolymers.com All Rights Reserved