Bhansali Engineering Santron IMS 2006 SAN Resin
| Category | Polymer , Thermoplastic , SAN Polymer , Styrene Acrylonitrile (SAN), Molded |
| Manufacturer | Bhansali Engineering |
| Trade Name | Santron |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Bhansali Engineering Santron IMS 2006 SAN Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Very High Rigidity Clear SANInformation provided by Bhansali
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.07 g/cc | 1.07 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.00400 - 0.00500 cm/cm | 0.00400 - 0.00500 in/in | ASTM D955 |
| Melt Flow | 30.0 g/10 min @Load 10.0 kg, Temperature 220 °C |
30.0 g/10 min @Load 22.0 lb, Temperature 428 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 124 | 124 | ASTM D785 |
| Tensile Strength, Yield | 78.5 MPa @Thickness 3.20 mm |
11400 psi @Thickness 0.126 in |
Type I, 5 mm/min; ASTM D638 |
| 83.4 MPa @Thickness 3.20 mm |
12100 psi @Thickness 0.126 in |
Type I, 50 mm/min; ASTM D638 | |
| Flexural Yield Strength | 113 MPa @Thickness 6.40 mm |
16400 psi @Thickness 0.252 in |
5 mm/min; ASTM D790 |
| Izod Impact, Notched | 0.392 J/cm @Thickness 3.20 mm |
0.735 ft-lb/in @Thickness 0.126 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 97.0 °C @Thickness 6.40 mm |
207 °F @Thickness 0.252 in |
Method A; ASTM D648 |
| Flammability, UL94 | HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Transmission, Visible | 90.0 % | 90.0 % | clear; thickness not quantified |
Users viewing this material also viewed the following:
- NOVA Chemicals Sclair® 56B4 HDPE Blow Molding Resin
- Overview of materials for Polybutylene Terephthalate (PBT), 20% Glass Fiber Filled
- Chevron Phillips HiD® 9075 HDPE Injection Molding Resin (discontinued **)
- Shakespeare HPA-40 diameter 0.5 mm PPS Monofilament
- Spartech Royalstatâ„¢ R675 PS Alloy Static Control Sheet
- SABIC Innovative Plastics LNP THERMOCOMP AF004L ABS
- Unipetrol PE HD LITEN® FB 29 HDPE
- A. Schulman POLYFORT™ FPP 1237 CaCO3 filled homopolymer polypropylene
- Covestro Baydur® 726 IBS Polyurethane Structural Foam RIM, Density 55 pcf, MDI-based 2-Component Liquid System
- Aremco Aremco-Bond™ 526N High Performance Epoxide
Copyright © lookpolymers.com All Rights Reserved