SABIC Innovative Plastics Valox® 357M PBT (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Valox® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Valox® 357M PBT (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
This data was supplied by SABIC-IP for the Asia Pacific region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.34 g/cc | 1.34 g/cc | ASTM D 792 |
| Water Absorption | 0.080 % @Time 86400 sec |
0.080 % @Time 24.0 hour |
ASTM D 570 |
| Linear Mold Shrinkage, Flow | 0.0080 - 0.011 cm/cm @Thickness 0.750 - 2.30 mm |
0.0080 - 0.011 in/in @Thickness 0.0295 - 0.0906 in |
SABIC Method |
| 0.010 - 0.014 cm/cm @Thickness 2.30 - 4.60 mm |
0.010 - 0.014 in/in @Thickness 0.0906 - 0.181 in |
SABIC Method | |
| Linear Mold Shrinkage, Transverse | 0.0090 - 0.013 cm/cm @Thickness 0.750 - 2.30 mm |
0.0090 - 0.013 in/in @Thickness 0.0295 - 0.0906 in |
SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 117 | 117 | ASTM D 785 |
| Tensile Strength at Break | 48.0 MPa | 6960 psi | Type I, 50 mm/min; ASTM D 638 |
| Tensile Strength, Yield | 48.0 MPa | 6960 psi | Type I, 50 mm/min; ASTM D 638 |
| Elongation at Break | 110 % | 110 % | Type I, 50 mm/min; ASTM D 638 |
| Flexural Strength | 82.0 MPa | 11900 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Flexural Yield Strength | 82.0 MPa | 11900 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Flexural Modulus | 2.06 GPa | 299 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Izod Impact, Notched | 5.30 J/cm @Temperature 23.0 °C |
9.93 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Izod Impact, Unnotched | 32.02 J/cm @Temperature 23.0 °C |
59.99 ft-lb/in @Temperature 73.4 °F |
ASTM D 4812 |
| Gardner Impact | 43.0 J @Temperature 23.0 °C |
31.7 ft-lb @Temperature 73.4 °F |
ASTM D 3029 |
| 43.0 J @Temperature 23.0 °C |
31.7 ft-lb @Temperature 73.4 °F |
ASTM D 3029 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 91.8 µm/m-°C @Temperature -40.0 - 40.0 °C |
51.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 124 µm/m-°C @Temperature 60.0 - 138 °C |
68.9 µin/in-°F @Temperature 140 - 280 °F |
ASTM E 831 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 137 °C @Thickness 6.40 mm |
279 °F @Thickness 0.252 in |
unannealed; ASTM D 648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 98.0 °C @Thickness 6.40 mm |
208 °F @Thickness 0.252 in |
unannealed; ASTM D 648 |
| UL RTI, Electrical | 120 °C | 248 °F | UL 746B |
| UL RTI, Mechanical with Impact | 120 °C | 248 °F | UL 746B |
| UL RTI, Mechanical without Impact | 140 °C | 284 °F | UL 746B |
| Flammability, UL94 | HB @Thickness 0.450 mm |
HB @Thickness 0.0177 in |
UL 94 by SABIC-IP |
| V-0 @Thickness 0.630 mm |
V-0 @Thickness 0.0248 in |
UL 94 by SABIC-IP | |
| 5VA @Thickness 2.99 mm |
5VA @Thickness 0.118 in |
UL 94 by SABIC-IP |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.20e+16 ohm-cm | >= 1.20e+16 ohm-cm | ASTM D 257 |
| Dielectric Constant | 3.2 @Frequency 100 Hz |
3.2 @Frequency 100 Hz |
ASTM D 150 |
| 3.2 @Frequency 1.00e+6 Hz |
3.2 @Frequency 1.00e+6 Hz |
ASTM D 150 | |
| Dielectric Strength | 18.5 kV/mm @Thickness 3.20 mm |
470 kV/in @Thickness 0.126 in |
in air; ASTM D 149 |
| 18.5 kV/mm @Thickness 3.20 mm |
470 kV/in @Thickness 0.126 in |
in oil; ASTM D 149 | |
| 25.1 kV/mm @Thickness 1.60 mm |
638 kV/in @Thickness 0.0630 in |
in oil; ASTM D 149 | |
| Dissipation Factor | 0.0030 @Frequency 100 Hz |
0.0030 @Frequency 100 Hz |
ASTM D 150 |
| 0.030 @Frequency 1.00e+6 Hz |
0.030 @Frequency 1.00e+6 Hz |
ASTM D 150 | |
| Arc Resistance | 60 - 120 sec | 60 - 120 sec | Tungsten, PLC code 6; ASTM D 495 |
| Comparative Tracking Index | 250 - 400 V | 250 - 400 V | PLC code 2; UL 746A |
| Hot Wire Ignition, HWI | 30 - 60 sec | 30 - 60 sec | PLC code 2; UL 746A |
| High Amp Arc Ignition, HAI | 15 - 30 arcs | 15 - 30 arcs | surface, PLC code 3; UL 746A |
| High Voltage Arc-Tracking Rate, HVTR | 80.0 - 150 mm/min | 3.15 - 5.91 in/min | PLC code 3; UL 746A |
| Descriptive Properties | Value | Comments |
|---|---|---|
| UV-light, water exposure/immersion | F2 | UL 746C |
Users viewing this material also viewed the following:
- OCTAL DPET™/PE Peelable Laminate Sheet
- ND Industries StudGrade® 131 Permanent CT Threadlocker
- M. Holland Company GS411 Polystyrene (discontinued **)
- Honeywell Aegis™ HCA95MP Nylon 6/6,6 Extrusion Grade Copolymer (discontinued **)
- Inno-Comp INNOPOL® CS 3-9230 KAR BU UV-Stabilized, 26% Mineral-Filled Compound Blend Of Polypropylene Homopolymer And Block-Copolymer
- A. Schulman POLYFORT™ FPP 1244 Mineral Filled, General Purpose Polypropylene
- DuPont Performance Polymers Crastin® HR5315HFS BK591 Polybutylene Terephthalate (PBT) (Unverified Data**)
- Barlog Plastics KEBAFLEX SG 65 A.01 TPE-S, Shore A65, natural
- Axiall 12880 Coax & Telecom Flexible PVC
- Atom Adhesives AA-BOND F110 Epoxy Adhesive
Copyright © lookpolymers.com All Rights Reserved