SABIC Innovative Plastics ULTEM SF2360 PEI Blend (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | ULTEM |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics ULTEM SF2360 PEI Blend (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
High flow Ultem for thin wall application
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.53 g/cc | 1.53 g/cc | ASTM D792 |
| Density | 1.53 g/cc | 0.0553 lb/in³ | ISO 1183 |
| Water Absorption | 0.10 % @Time 86400 sec |
0.10 % @Time 24.0 hour |
ISO 62-1 |
| Moisture Absorption | 0.0400 % | 0.0400 % | 23°C / 50% RH |
| Linear Mold Shrinkage, Flow | 0.0039 cm/cm | 0.0039 in/in | SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0047 cm/cm | 0.0047 in/in | SABIC Method |
| Melt Flow | 18 g/10 min @Load 6.60 kg, Temperature 337 °C |
18 g/10 min @Load 14.6 lb, Temperature 639 °F |
ASTM D1238 |
| Melt Index of Compound | 40 g/10 min @Load 10.0 kg, Temperature 345 °C |
40 g/10 min @Load 22.0 lb, Temperature 653 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 148 MPa | 21500 psi | Type I, 5 mm/min; ASTM D638 |
| 152 MPa | 22000 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 2.0 % | 2.0 % | Type I, 5 mm/min; ASTM D638 |
| 2.0 % | 2.0 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 11.95 GPa | 1733 ksi | 5 mm/min; ASTM D638 |
| Flexural Yield Strength | 212 MPa | 30700 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 9.94 GPa | 1440 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 9.94 GPa | 1440 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.890 J/cm | 1.67 ft-lb/in | ASTM D256 |
| Izod Impact, Notched (ISO) | 9.00 kJ/m² | 4.28 ft-lb/in² | 80*10*4; ISO 180/1A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 13.0 µm/m-°C @Temperature 23.0 - 150 °C |
7.22 µin/in-°F @Temperature 73.4 - 302 °F |
ISO 11359-2 |
| 15.0 µm/m-°C @Temperature -40.0 - 150 °C |
8.33 µin/in-°F @Temperature -40.0 - 302 °F |
ASTM E 831 | |
| CTE, linear, Transverse to Flow | 54.0 µm/m-°C @Temperature -40.0 - 150 °C |
30.0 µin/in-°F @Temperature -40.0 - 302 °F |
ASTM E 831 |
| 62.0 µm/m-°C @Temperature 23.0 - 150 °C |
34.4 µin/in-°F @Temperature 73.4 - 302 °F |
ISO 11359-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 208 °C | 406 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| 203 °C @Thickness 3.20 mm |
397 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Flammability, UL94 | V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
UL 94 by SABIC-IP |
Users viewing this material also viewed the following:
- ND Industries 621 Heptane-Acetone SuperGlue accelerator
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 60 PHR N650 Filler
- Mallard Creek Polymers Rovene® 6015 Acrylic Emulsion
- Global GPEI-210 10% Glass Filled Reinforced, Polyetherimide
- Mitsui UNISTOLEâ„¢ R-100K Polyolefinic Primer/ Adhesive
- SABIC Innovative Plastics NORYL SE100HX PPE+PS
- SABIC Innovative Plastics LNP THERMOCOMP KF004AL Acetal Homopolymer
- Tipco Tipcolene® FPW 35 - 35% Wollastonite Reinforced Polypropylene Homopolymer, High Heat Stability
- Azoty Tarnow™ TARFLEN SM-B30 PTFE
- 3M Dyneon™ PVDF 31008/0009 Polyvinylidene Fluoride (discontinued **)
Copyright © lookpolymers.com All Rights Reserved