SABIC Innovative Plastics ULTEM 9085 PEI Blend (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | ULTEM |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics ULTEM 9085 PEI Blend (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
High flow Polyetherimide blend. Meets FAR 25.853 and OSU 65/65 with low toxicity, smoke and flame evolution.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.34 g/cc | 1.34 g/cc | ASTM D792 |
| Density | 1.34 g/cc | 0.0484 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.170 % | 0.170 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.39 % | 0.39 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 8.9 g/10 min @Load 6.60 kg, Temperature 295 °C |
8.9 g/10 min @Load 14.6 lb, Temperature 563 °F |
ASTM D1238 |
| Melt Index of Compound | 65 g/10 min @Load 5.00 kg, Temperature 360 °C |
65 g/10 min @Load 11.0 lb, Temperature 680 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 71.0 MPa | 10300 psi | 5 mm/min; ISO 527 |
| 74.0 MPa | 10700 psi | Type I, 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 84.0 MPa | 12200 psi | Type I, 5 mm/min; ASTM D638 |
| 88.0 MPa | 12800 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 50 % | 50 % | 5 mm/min; ISO 527 |
| 72 % | 72 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 6.7 % | 6.7 % | 5 mm/min; ISO 527 |
| 7.0 % | 7.0 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 3.05 GPa | 442 ksi | 1 mm/min; ISO 527 |
| 3.44 GPa | 499 ksi | 5 mm/min; ASTM D638 | |
| Flexural Yield Strength | 90.0 MPa | 13100 psi | 2 mm/min; ISO 178 |
| 138 MPa | 20000 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 2.75 GPa | 399 ksi | 2 mm/min; ISO 178 |
| 2.92 GPa | 424 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 1.15 J/cm | 2.15 ft-lb/in | ASTM D256 |
| Izod Impact, Notched (ISO) | 13.0 kJ/m² | 6.19 ft-lb/in² | 80*10*4; ISO 180/1A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 152 °C | 306 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 153 °C @Thickness 3.20 mm |
307 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 173 °C | 343 °F | Rate B/120; ISO 306 |
| Oxygen Index | 49 % | 49 % | ASTM D2863 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| FAA Flammability, FAR 25.853 A/B | <5 | FAR 25.853 |
| OSU total heat release (2 minute test) | 16kW-min/m^2 | FAR 25.853 |
| OSU peak heat release rate (5 minute test) | 36kW/m^2 | FAR 25.853 |
| Vertical Burn a (60s) passes at | 2sec | FAR 25.853 |
Users viewing this material also viewed the following:
- NOVA Chemicals Gedexcel® 54B Expandable Polystyrene
- Karina E 701D02/128-SD Yellow PVC Compound
- Shamrock Technologies Fluoro FR-150 Anti-dripping Thermoplastic Grade PTFE Additive
- Shinkong Synthetic Fibers Shinite® D201K011 PBT, Super Viscosity
- Vyncolit 2950 W Novolac Phenolic
- Epoxy Technology EPO-TEK® EK1000 Epoxy
- 3M Safety-Walk™ 370 Gray Slip-Resistant Medium Resilient Tapes and Treads
- DuPont Performance Polymers Zytel® FR50 BK505 Nylon 66 (Unverified Data**)
- Ineos Nova Zylar® 535 Clear Impact Modified Acrylic Copolymer (discontinued **)
Copyright © lookpolymers.com All Rights Reserved