SABIC Innovative Plastics ULTEM 9076 PEI
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | ULTEM |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics ULTEM 9076 PEI.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Standard flow Polyetherimide Blend. Meets FAR 25.853 and OSU 65/65 with low toxicity, smoke, and flame evolution. ECO Conforming.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.30 g/cc | 1.30 g/cc | ASTM D792 |
| Halogen Content | 0.00 % | 0.00 % | SABIC Method |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 1.4 g/10 min @Load 6.60 kg, Temperature 295 °C |
1.4 g/10 min @Load 14.6 lb, Temperature 563 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 96.0 MPa | 13900 psi | Type I, 5 mm/min; ASTM D638 |
| Elongation at Break | 92 % | 92 % | Type I, 5 mm/min; ASTM D638 |
| Tensile Modulus | 3.30 GPa | 479 ksi | 5 mm/min; ASTM D638 |
| Flexural Strength | 141 MPa | 20500 psi | 2.6 mm/min, 100 mm span; ASTM D790 |
| Flexural Yield Strength | 144 MPa | 20900 psi | 2.6 mm/min, 100 mm span; ASTM D790 |
| Flexural Modulus | 3.24 GPa | 470 ksi | 2.6 mm/min, 100 mm span; ASTM D790 |
| Izod Impact, Notched | 0.740 J/cm | 1.39 ft-lb/in | ASTM D256 |
| 21.36 J/cm @Thickness 3.20 mm |
40.02 ft-lb/in @Thickness 0.126 in |
ASTM D256 | |
| Gardner Impact | 35.0 J | 25.8 ft-lb | ASTM D3029 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 188 °C @Thickness 6.40 mm |
370 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| FAA Flammability, FAR 25.853 A/B | SECT A-1 | FAR 25.853 |
| OSU total heat release (2 minute test) | 10kW-min/m^2 | FAR 25.853 |
| Vertical Burn a (60s) passes at | 1sec | FAR 25.853 |
| Vertical Burn b (12s) passes at | 0sec | FAR 25.853 |
Users viewing this material also viewed the following:
- Osprey Metals 49FeCo2V Cobalt Alloy Powder (Grade 80% - 22)
- Plansee Cu-MoCu-Cu Laminate
- Parker Chomerics CHO-BOND 2165 Polyurethane Sealant
- SABIC Innovative Plastics LNP LUBRICOMP QAP22S PA6.10
- Styron Pulse® 710 ABS + Polycarbonate
- Dow Corning SYL-OFF® 7678 CROSSLINKER
- Clariant Renol TPU1088A Polyurethane Elastomer, Aromatic Polyester
- Abatron Acrylic 57-1™ Clear, Water-Based Coating
- DuPont Performance Polymers Hypalon® 30 Chlorosulfonated Polyethylene Rubber, Carbon Black Filled Compound (d
Copyright © lookpolymers.com All Rights Reserved