SABIC Innovative Plastics ULTEM 4000 PEI (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | ULTEM |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics ULTEM 4000 PEI (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Glass fiber, PTFE, and Graphite filled, standard flow Polyetherimide (Tg 217C). Resin is RoHS compliant. UL94 V0 listing.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.68 g/cc | 0.0607 lb/in³ | ISO 1183 |
| Moisture Absorption | 0.300 % | 0.300 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.70 % | 0.70 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0030 cm/cm | 0.0010 - 0.0030 in/in | on Tensile Bar; SABIC Method |
| Melt Index of Compound | 5.0 g/10 min @Load 5.00 kg, Temperature 360 °C |
5.0 g/10 min @Load 11.0 lb, Temperature 680 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, H358/30 | 140 MPa | 20300 psi | ISO 2039-1 |
| Tensile Strength at Break | 90.0 MPa | 13100 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 1.0 % | 1.0 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 9.90 GPa | 1440 ksi | 1 mm/min; ISO 527 |
| Flexural Strength | 120 MPa | 17400 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 7.00 GPa | 1020 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Unnotched (ISO) | 15.0 kJ/m² | 7.14 ft-lb/in² | 80*10*4; ISO 180/1U |
| 15.0 kJ/m² @Temperature -30.0 °C |
7.14 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1U | |
| Charpy Impact, Notched | 0.800 J/cm² | 3.81 ft-lb/in² | ISO 179/2C |
| 0.800 J/cm² @Temperature -30.0 °C |
3.81 ft-lb/in² @Temperature -22.0 °F |
ISO 179/2C | |
| K (wear) Factor | 24.2 x 10-8 mm³/N-M | 12.0 x 10-10 in³-min/ft-lb-hr | PV=2000 psi-fpm vs Self; SABIC Method |
| 765 x 10-8 mm³/N-M | 380 x 10-10 in³-min/ft-lb-hr | PV=2000 psi-fpm vs Self; SABIC Method | |
| Limiting Pressure Velocity | 2.30 MPa-m/sec | 65700 psi-ft/min | 0.51 m/s; SABIC Method |
| Taber Abrasion, mg/1000 Cycles | 30 | 30 | CS-17, 1 kg; SABIC Method |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 15.0 µm/m-°C @Temperature 23.0 - 150 °C |
8.33 µin/in-°F @Temperature 73.4 - 302 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 50.0 µm/m-°C @Temperature 23.0 - 150 °C |
27.8 µin/in-°F @Temperature 73.4 - 302 °F |
ISO 11359-2 |
| Thermal Conductivity | 0.430 W/m-K | 2.98 BTU-in/hr-ft²-°F | ISO 8302 |
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | Edgew 120*10*4 sp=100mm; ISO 75/Be |
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| Vicat Softening Point | 215 °C | 419 °F | Rate B/50; ISO 306 |
| 220 °C | 428 °F | Rate B/120; ISO 306 | |
| 225 °C | 437 °F | Rate A/50; ISO 306 | |
| Glass Transition Temp, Tg | 217 °C | 423 °F | |
| UL RTI, Electrical | 105 °C | 221 °F | UL 746B |
| UL RTI, Mechanical with Impact | 105 °C | 221 °F | UL 746B |
| UL RTI, Mechanical without Impact | 105 °C | 221 °F | UL 746B |
| Flammability, UL94 | V-0 @Thickness 0.840 mm |
V-0 @Thickness 0.0331 in |
UL 94 |
| Oxygen Index | 48 % | 48 % | ISO 4589 |
| Glow Wire Test | 960 °C @Thickness 3.20 mm |
1760 °F @Thickness 0.126 in |
IEC 60695-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | ROA; IEC 60093 |
| Dielectric Constant | 6.2 @Frequency 1.00e+6 Hz |
6.2 @Frequency 1.00e+6 Hz |
IEC 60250 |
| 6.8 @Frequency 50.0 - 60.0 Hz |
6.8 @Frequency 50.0 - 60.0 Hz |
IEC 60250 | |
| Dissipation Factor | 0.013 @Frequency 50.0 - 60.0 Hz |
0.013 @Frequency 50.0 - 60.0 Hz |
IEC 60250 |
| 0.022 @Frequency 1.00e+6 Hz |
0.022 @Frequency 1.00e+6 Hz |
IEC 60250 | |
| Comparative Tracking Index | >= 100 V | >= 100 V | IEC 60112 |
| 200 V | 200 V | IEC 60112 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Ball Pressure Test, 125°C +/- 2°C | PASSES | IEC 60695-10-2 |
Users viewing this material also viewed the following:
- MV Labs PD780 [Pd(NH3)4](NO3)2 Tetraminepalladium(II) nitrate
- Freudenberg Simrit Viton® SC1106 CV75 HP-1 (TFE/P)
- Taiwan Sheen Soon Sheenthane® AH-591 TPU for Hotmelt Adhesive
- Teknor Apex APEX® 90-A471R-80-NT Polyvinyl Chloride, Flexible
- TIMCAL TIMREX® 20X50 mesh Natural Flake Graphite
- Williams Advanced Alloys Wambraze™ WB853 Solder
- ExxonMobil Exxtral™ LNV 010 Performance Polyolefin
- Dow Corning 1593 CLEANER/PRIMER
- ACC MM816 Low Tear Condensation Cure 2-Part Molding Rubber
- BASF Ultramid® 8253 BK-102 PA6 (Dry)
Copyright © lookpolymers.com All Rights Reserved