SABIC Innovative Plastics ULTEM 2310 PEI
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | ULTEM |
| Port | Ningbo port,China |
| Trade Terms | EXW, FOB, CFR, CIF |
| Payment Terms | L/C, T/T, PayPal |
| Download PDF | SABIC Innovative Plastics ULTEM 2310 PEI.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
30% Glass fiber filled, enhanced flow Polyetherimide (Tg 217C). ECO Conforming, UL94 V0 and 5VA listing.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.51 g/cc | 1.51 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0040 cm/cm <br>@Thickness 3.20 mm |
0.0020 - 0.0040 in/in <br>@Thickness 0.126 in |
SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0020 - 0.0040 cm/cm <br>@Thickness 3.20 mm |
0.0020 - 0.0040 in/in <br>@Thickness 0.126 in |
SABIC Method |
| Melt Flow | 7.6 g/10 min <br>@Load 6.60 kg,<br> Temperature 337 °C |
7.6 g/10 min <br>@Load 14.6 lb,<br> Temperature 639 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 158 MPa | 22900 psi | Type I, 5 mm/min; ASTM D638 |
| Tensile Strength, Yield | 168 MPa | 24400 psi | Type I, 5 mm/min; ASTM D638 |
| Elongation at Break | 2.0 % | 2.0 % | Type I, 5 mm/min; ASTM D638 |
| Tensile Modulus | 9.23 GPa | 1340 ksi | 5 mm/min; ASTM D638 |
| Flexural Strength | 220 MPa | 31900 psi | 2.6 mm/min, 100 mm span; ASTM D790 |
| Flexural Modulus | 9.23 GPa | 1340 ksi | 2.6 mm/min, 100 mm span; ASTM D790 |
| Izod Impact, Notched | 0.850 J/cm | 1.59 ft-lb/in | ASTM D256 |
| 4.37 J/cm <br>@Thickness 3.20 mm |
8.19 ft-lb/in <br>@Thickness 0.126 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 16.2 µm/m-°C <br>@Temperature -20.0 - 150 °C |
9.00 µin/in-°F <br>@Temperature -4.00 - 302 °F |
ASTM E 831 |
| CTE, linear, Transverse to Flow | 41.4 µm/m-°C <br>@Temperature -20.0 - 150 °C |
23.0 µin/in-°F <br>@Temperature -4.00 - 302 °F |
ASTM E 831 |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C <br>@Thickness 6.40 mm |
410 °F <br>@Thickness 0.252 in |
unannealed; ASTM D648 |
| Glass Transition Temp, Tg | 217 °C | 423 °F | |
| UL RTI, Electrical | 180 °C | 356 °F | UL 746B |
| UL RTI, Mechanical with Impact | 170 °C | 338 °F | UL 746B |
| UL RTI, Mechanical without Impact | 180 °C | 356 °F | UL 746B |
| Flammability, UL94 | V-0 <br>@Thickness 0.250 mm |
V-0 <br>@Thickness 0.00984 in |
UL 94 |
| 5VA <br>@Thickness 1.21 mm |
5VA <br>@Thickness 0.0476 in |
UL 94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Arc Resistance | 60 - 120 sec | 60 - 120 sec | Tungsten; ASTM D495 |
| Comparative Tracking Index | 100 - 175 V | 100 - 175 V | UL 746A |
| Hot Wire Ignition, HWI | 60 - 120 sec | 60 - 120 sec | UL 746A |
| High Amp Arc Ignition, HAI | 0.00 - 15 arcs | 0.00 - 15 arcs | UL 746A |
| High Voltage Arc-Tracking Rate, HVTR | 80.0 - 150 mm/min | 3.15 - 5.91 in/min | UL 746A |
Users viewing this material also viewed the following:
- MV Labs SC870 Sc2(C2O4)3·5H2O Scandium oxalate hydrate
- Premix Premi-Glas® 3101-22 Fiberglass Reinforced Thermoset BMC
- Nilit FRIANYL A63 S15 Nylon 6.6 for injection molding
- PTS Tristar® PC-10R-(6) 6 MFI Polycarbonate With Release
- Materion ToughMet® T3 AT110 (OD≥4")
- H.C. Starck Grade I Amorphous Boron
- Hexcel® HexPly® ES 84 120°C Curing Epoxy Matrix, E-glass Balanced fabric 390 g/m2
- Fainplast Compounds CL 80/1 Flexible PVC, Sheathing
- Addcomp ADD-VANCE® THC 723 PP based masterbatch containing heat stabilizers, coupling agent and carbon black
- BASF Ultramid® C3U BK 23079 PA6/66 FR (Conditioned)
Copyright © lookpolymers.com All Rights Reserved