SABIC Innovative Plastics ULTEM 2200F PEI
| Category | Polymer , Thermoplastic , Polyetherimide (PEI) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | ULTEM |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics ULTEM 2200F PEI.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
20% Glass fiber filled, standard flow Polyetherimide (Tg 217C). ECO Conforming. US FDA Food Contact compliant in recognized colors.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.42 g/cc | 1.42 g/cc | ASTM D792 |
| Density | 1.42 g/cc | 0.0513 lb/in³ | ISO 1183 |
| Water Absorption | 0.19 % @Time 86400 sec |
0.19 % @Time 24.0 hour |
ASTM D570 |
| Moisture Absorption | 0.550 % | 0.550 % | 23°C / 50% RH; ISO 62 |
| Moisture Absorption at Equilibrium | 1.1 % | 1.1 % | ASTM D570 |
| Water Absorption at Saturation | 1.0 % | 1.0 % | ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0030 - 0.0050 cm/cm @Thickness 3.20 mm |
0.0030 - 0.0050 in/in @Thickness 0.126 in |
SABIC Method |
| Linear Mold Shrinkage, Transverse | 0.0030 - 0.0050 cm/cm @Thickness 3.20 mm |
0.0030 - 0.0050 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 6.0 g/10 min @Load 6.60 kg, Temperature 337 °C |
6.0 g/10 min @Load 14.6 lb, Temperature 639 °F |
ASTM D1238 |
| Melt Index of Compound | 7.0 g/10 min @Load 5.00 kg, Temperature 360 °C |
7.0 g/10 min @Load 11.0 lb, Temperature 680 °F |
MVR [cm^3/10 min]; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 114 | 114 | ASTM D785 |
| Tensile Strength at Break | 131 MPa | 19000 psi | Type I, 5 mm/min; ASTM D638 |
| 131 MPa | 19000 psi | 5 mm/min; ISO 527 | |
| Tensile Strength, Yield | 131 MPa | 19000 psi | Type I, 5 mm/min; ASTM D638 |
| 131 MPa | 19000 psi | 5 mm/min; ISO 527 | |
| Elongation at Break | 4.0 % | 4.0 % | Type I, 5 mm/min; ASTM D638 |
| 4.0 % | 4.0 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 4.0 % | 4.0 % | Type I, 5 mm/min; ASTM D638 |
| 4.0 % | 4.0 % | 5 mm/min; ISO 527 | |
| Tensile Modulus | 6.89 GPa | 999 ksi | 5 mm/min; ASTM D638 |
| 6.89 GPa | 999 ksi | 1 mm/min; ISO 527 | |
| Flexural Yield Strength | 225 MPa | 32600 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 228 MPa | 33100 psi | 2 mm/min; ISO 178 | |
| Flexural Modulus | 6.85 GPa | 994 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 6.89 GPa | 999 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.640 J/cm | 1.20 ft-lb/in | ASTM D256 |
| 0.700 J/cm @Temperature -30.0 °C |
1.31 ft-lb/in @Temperature -22.0 °F |
ASTM D256 | |
| 4.64 J/cm @Thickness 3.20 mm |
8.69 ft-lb/in @Thickness 0.126 in |
ASTM D256 | |
| Izod Impact, Unnotched | 4.80 J/cm | 8.99 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 64.0 kJ/m² | 30.5 ft-lb/in² | 80*10*4; ISO 180/1A |
| 70.0 kJ/m² @Temperature -30.0 °C |
33.3 ft-lb/in² @Temperature -22.0 °F |
80*10*4; ISO 180/1A | |
| Charpy Impact, Notched | 6.50 J/cm² | 30.9 ft-lb/in² | Edgew 80*10*4 sp=62mm; ISO 179/1eA |
| Dart Drop, Total Energy | 8.00 J @Temperature 23.0 °C |
5.90 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 25.0 µm/m-°C @Temperature -20.0 - 150 °C |
13.9 µin/in-°F @Temperature -4.00 - 302 °F |
ASTM E 831 |
| 25.0 µm/m-°C @Temperature 23.0 - 150 °C |
13.9 µin/in-°F @Temperature 73.4 - 302 °F |
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 50.0 µm/m-°C @Temperature -40.0 - 150 °C |
27.8 µin/in-°F @Temperature -40.0 - 302 °F |
ASTM E 831 |
| 50.0 µm/m-°C @Temperature 23.0 - 150 °C |
27.8 µin/in-°F @Temperature 73.4 - 302 °F |
ISO 11359-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | Edgew 120*10*4 sp=100mm; ISO 75/Ae |
| 208 °C @Thickness 3.20 mm |
406 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Vicat Softening Point | 212 °C | 414 °F | Rate B/50; ISO 306 |
| 218 °C | 424 °F | Rate B/120; ISO 306 | |
| 220 °C | 428 °F | Rate B/50; ASTM D1525 | |
| Glass Transition Temp, Tg | 217 °C | 423 °F | |
| Oxygen Index | 50 % | 50 % | ASTM D2863 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 7.00e+16 ohm-cm | 7.00e+16 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.5 @Frequency 1000 Hz |
3.5 @Frequency 1000 Hz |
ASTM D150 |
| Dielectric Strength | 26.3 kV/mm @Thickness 1.60 mm |
668 kV/in @Thickness 0.0630 in |
in oil; ASTM D149 |
| Dissipation Factor | 0.0015 @Frequency 1000 Hz |
0.0015 @Frequency 1000 Hz |
ASTM D150 |
| 0.0049 @Frequency 2.45e+9 Hz |
0.0049 @Frequency 2.45e+9 Hz |
ASTM D150 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Ball Pressure Test, 125°C +/- 2°C | Passes | IEC 60695-10-2 |
Users viewing this material also viewed the following:
- S&E Specialty Polymers GTPO8290-GT7 PVC
- LyondellBasell Lupolen® 3026 F LDPE, Film Grade
- GEHR Plastics PA 6 C Nylon 6 Cast
- SABIC Innovative Plastics LNP THERMOCOMP EC006APQ PEI
- Tra-Con Tra-Cast FS255 Flexible Clear Epoxy Casting Compound
- DSM Akulon® S223-D Nylon 66 (European Grade) (Dry)
- Daelim H&L Plavis-G40 DF 40% Graphite Filled Aromatic Polyimide Bearing
- Dow DOWLEX™ 2078G Linear Low Density Polyethylene
- Arlon 51N Lead-Free Compatible Epoxy Low-Flow
- Fainplast Compounds KLT 79 Flexible PVC, Insulation Transparent Cables Lead Free
Copyright © lookpolymers.com All Rights Reserved