SABIC Innovative Plastics ULTEM 1000R PEI

Category Polymer , Thermoplastic , Polyetherimide (PEI)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name ULTEM
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics ULTEM 1000R PEI.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Standard flow Polyetherimide (Tg 217C) with internal mold release. ECO Conforming, UL94 V0, V2 and 5VA listing.
Physical Properties Metric English Comments
Specific Gravity 1.27 g/cc
1.27 g/cc
ASTM D792
Water Absorption 0.25 %

@Time 86400 sec
 0.25 %

@Time 24.0 hour
 ASTM D570
Moisture Absorption at Equilibrium 1.25 %
1.25 %
ASTM D570
Linear Mold Shrinkage, Flow 0.0050 - 0.0070 cm/cm

@Thickness 3.20 mm
 0.0050 - 0.0070 in/in

@Thickness 0.126 in
 SABIC Method
Melt Flow 9.7 g/10 min

@Load 6.60 kg,
Temperature 337 °C
 9.7 g/10 min

@Load 14.6 lb,
Temperature 639 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell M 109
109
ASTM D785
Tensile Strength, Yield 110 MPa
16000 psi
Type I, 5 mm/min; ASTM D638
Elongation at Break 60 %
60 %
Type I, 5 mm/min; ASTM D638
Elongation at Yield 7.0 %
7.0 %
Type I, 5 mm/min; ASTM D638
Tensile Modulus 3.58 GPa
519 ksi
5 mm/min; ASTM D638
Flexural Yield Strength 165 MPa
23900 psi
2.6 mm/min, 100 mm span; ASTM D790
Flexural Modulus 3.51 GPa
509 ksi
2.6 mm/min, 100 mm span; ASTM D790
Poissons Ratio 0.36
0.36
ASTM E 132
Izod Impact, Notched 0.530 J/cm
0.993 ft-lb/in
ASTM D256
16.02 J/cm

@Thickness 3.20 mm
 30.01 ft-lb/in

@Thickness 0.126 in
 ASTM D256
Izod Impact, Unnotched 13.35 J/cm
25.01 ft-lb/in
ASTM D4812
Gardner Impact 36.0 J
26.6 ft-lb
ASTM D3029
Taber Abrasion, mg/1000 Cycles 10
10
CS-17, 1 kg; ASTM D1044
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 55.8 µm/m-°C

@Temperature -20.0 - 150 °C
 31.0 µin/in-°F

@Temperature -4.00 - 302 °F
 ASTM E 831
CTE, linear, Transverse to Flow 54.0 µm/m-°C

@Temperature -20.0 - 150 °C
 30.0 µin/in-°F

@Temperature -4.00 - 302 °F
 ASTM E 831
Thermal Conductivity 0.220 W/m-K
1.53 BTU-in/hr-ft²-°F
ASTM C177
Deflection Temperature at 0.46 MPa (66 psi) 210 °C

@Thickness 6.40 mm
 410 °F

@Thickness 0.252 in
 unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 201 °C

@Thickness 6.40 mm
 394 °F

@Thickness 0.252 in
 unannealed; ASTM D648
Vicat Softening Point 218 °C
424 °F
Rate B/50; ASTM D1525
Glass Transition Temp, Tg 217 °C
423 °F
UL RTI, Electrical 170 °C
338 °F
UL 746B
UL RTI, Mechanical with Impact 170 °C
338 °F
UL 746B
UL RTI, Mechanical without Impact 170 °C
338 °F
UL 746B
Flammability, UL94 V-2

@Thickness 0.400 mm
 V-2

@Thickness 0.0157 in
 UL 94
V-0

@Thickness 0.750 mm
 V-0

@Thickness 0.0295 in
 UL 94
5VA

@Thickness 3.00 mm
 5VA

@Thickness 0.118 in
 UL 94
Oxygen Index 47 %
47 %
ASTM D2863
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+17 ohm-cm
1.00e+17 ohm-cm
ASTM D257
Dielectric Constant 3.15

@Frequency 1000 Hz
 3.15

@Frequency 1000 Hz
 ASTM D150
Dielectric Strength 28.0 kV/mm

@Thickness 1.60 mm
 711 kV/in

@Thickness 0.0630 in
 in oil; ASTM D149
32.7 kV/mm

@Thickness 1.60 mm
 831 kV/in

@Thickness 0.0630 in
 in air; ASTM D149
Dissipation Factor 0.0013

@Frequency 1000 Hz
 0.0013

@Frequency 1000 Hz
 ASTM D150
0.0025

@Frequency 2.45e+9 Hz
 0.0025

@Frequency 2.45e+9 Hz
 ASTM D150
Arc Resistance 120 - 180 sec
120 - 180 sec
Tungsten; ASTM D495
Comparative Tracking Index 100 - 175 V
100 - 175 V
UL 746A
Hot Wire Ignition, HWI 60 - 120 sec
60 - 120 sec
UL 746A
High Amp Arc Ignition, HAI 15 - 30 arcs
15 - 30 arcs
UL 746A
High Voltage Arc-Tracking Rate, HVTR 25.4 - 80.0 mm/min
1.00 - 3.15 in/min
UL 746A
Descriptive Properties Value Comments
NBS Smoke Density, Flaming, Ds 4 min 0.7
ASTM E 662
Users viewing this material also viewed the following: