| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | SABIC STAMAX |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics SABIC STAMAX 30YM240 PP.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
SABIC® STAMAX 30YM240 is a 30% long glass fiber reinforced polypropylene. The glass fibers are chemically coupled to the PP matrix, resulting in high stiffness and strength. The IMDS is 16496906.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.13 g/cc | 1.13 g/cc | ASTM D792 |
| Density | 1.12 g/cc | 0.0405 lb/in³ | ISO 1183 |
| Filler Content | 30 % | 30 % | glass; ISO 3451 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 97.0 MPa | 14100 psi | Type I, 50 mm/min; ASTM D638 |
| 110 MPa | 16000 psi | 50 mm/min, 1A; ISO 527 | |
| 51.0 MPa @Temperature 120 °C |
7400 psi @Temperature 248 °F |
50 mm/min, 1A; ISO 527 | |
| 70.0 MPa @Temperature 80.0 °C |
10200 psi @Temperature 176 °F |
50 mm/min, 1A; ISO 527 | |
| Elongation at Break | 2.0 % | 2.0 % | Type I, 50 mm/min; ASTM D638 |
| 2.3 % | 2.3 % | 50 mm/min; ISO 527 | |
| Tensile Modulus | 6.65 GPa | 965 ksi | 1 mm/min; ISO 527 |
| 6.69 GPa | 970 ksi | 50 mm/min; ASTM D638 | |
| 3.50 GPa @Temperature 120 °C |
508 ksi @Temperature 248 °F |
1 mm/min; ISO 527 | |
| 4.60 GPa @Temperature 80.0 °C |
667 ksi @Temperature 176 °F |
1 mm/min; ISO 527 | |
| Flexural Modulus | 5.79 GPa | 840 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 5.90 GPa | 856 ksi | 2 mm/min, 64mm span; ISO 178 | |
| 4.20 GPa @Temperature 80.0 °C |
609 ksi @Temperature 176 °F |
2 mm/min, 64mm span; ISO 178 | |
| Izod Impact, Notched (ISO) | 15.0 kJ/m² | 7.14 ft-lb/in² | 80*10*4mm, Cut; ISO 180/1A |
| Charpy Impact, Notched | 1.90 J/cm² | 9.04 ft-lb/in² | 80*10*4mm, Cut; ISO 179/1eA |
| 2.50 J/cm² @Temperature -30.0 °C |
11.9 ft-lb/in² @Temperature -22.0 °F |
80*10*4mm, Cut; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 156 °C | 313 °F | 80*10*4mm, Cut; ISO 75-1&2 |
| 158 °C @Thickness 3.20 mm |
316 °F @Thickness 0.126 in |
ASTM D648 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Cycoloy® CY5220 PC+ABS (Asia Pacific)
- Albis Plastics Cellulose Acetate Propionate CP808 (FDA), 10% Plasticizer (discontinued **)
- Kuraray SEPTON® S8007 Thermoplastic Rubber
- Lanxess Durethan® AKV 15 H2.0 901510 Nylon 66, 15% Glass Fiber
- Shandong Dongyue Polymer DF-21C PTFE Presintered Resin
- SABIC Innovative Plastics LNP Thermocomp AF002L ABS (Asia Pacific)
- Sharadaa Ceramics ZAP 011 Smart Cast Application
- BASF Pluracol® 1158 Specialty Polyol
- ATI Allegheny Ludlum Stainless Steel Free Machining Grade Type 303, Annealed (UNS S30300)
- DuPont Performance Polymers Hypalon® 40S Chlorosulfonated Polyethylene Rubber, Peroxide Cured Carbon Black Filled Compound
Copyright © lookpolymers.com All Rights Reserved