SABIC Innovative Plastics Noryl N1251 PPE+PS
| Category | Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Noryl |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Noryl N1251 PPE+PS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
ECO-FLO(tm). ECO conforming, non-halogen flame retardant PPE+PS. High flow. Electrical and Business Equipment applications.This data was supplied by SABIC-IP for the Americas region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.10 g/cc | 1.10 g/cc | ASTM D 792 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 9.0 g/10 min @Load 5.00 kg, Temperature 280 °C |
9.0 g/10 min @Load 11.0 lb, Temperature 536 °F |
ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 53.0 MPa | 7690 psi | Type I, 50 mm/min; ASTM D 638 |
| Tensile Strength, Yield | 64.0 MPa | 9280 psi | Type I, 50 mm/min; ASTM D 638 |
| Elongation at Break | 20 % | 20 % | Type I, 50 mm/min; ASTM D 638 |
| Elongation at Yield | 4.2 % | 4.2 % | Type I, 50 mm/min; ASTM D 638 |
| Tensile Modulus | 2.49 GPa | 361 ksi | 50 mm/min; ASTM D 638 |
| Flexural Yield Strength | 97.0 MPa | 14100 psi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Flexural Modulus | 2.48 GPa | 360 ksi | 1.3 mm/min, 50 mm span; ASTM D 790 |
| Izod Impact, Notched | 2.13 J/cm @Temperature 23.0 °C |
3.99 ft-lb/in @Temperature 73.4 °F |
ASTM D 256 |
| Impact Test | 45.0 J @Temperature 23.0 °C |
33.2 ft-lb @Temperature 73.4 °F |
Instrumented Impact Total Energy; ASTM D 3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 64.8 µm/m-°C @Temperature -40.0 - 40.0 °C |
36.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| CTE, linear, Transverse to Flow | 72.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
40.0 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| Deflection Temperature at 0.46 MPa (66 psi) | 131 °C @Thickness 3.20 mm |
268 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| 134 °C @Thickness 6.40 mm |
273 °F @Thickness 0.252 in |
unannealed; ASTM D 648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 116 °C @Thickness 3.20 mm |
241 °F @Thickness 0.126 in |
unannealed; ASTM D 648 |
| 123 °C @Thickness 6.40 mm |
253 °F @Thickness 0.252 in |
unannealed; ASTM D 648 | |
| Vicat Softening Point | 136 °C | 277 °F | Rate B/50; ASTM D 1525 |
| UL RTI, Electrical | 65.0 °C | 149 °F | UL 746B |
| UL RTI, Mechanical with Impact | 65.0 °C | 149 °F | UL 746B |
| UL RTI, Mechanical without Impact | 65.0 °C | 149 °F | UL 746B |
| Flammability, UL94 | V-1 @Thickness 1.49 mm |
V-1 @Thickness 0.0587 in |
UL 94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Comparative Tracking Index | 250 - 400 V | 250 - 400 V | PLC code 2; UL 746A |
| Hot Wire Ignition, HWI | 60 - 120 sec | 60 - 120 sec | PLC code 1; UL 746A |
| High Amp Arc Ignition, HAI | >= 120 arcs | >= 120 arcs | surface, PLC code 0; UL 746A |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Cycolac® INP572 ABS
- Westlake Plastics Propylux® SD-X7 Polypropylene (static dissipative)
- China Tungsten YG25C Tungsten Carbide
- EMS-Grivory Grivory® GVX-6 H black 9915 PA*-GF60
- Arkema Group Lucalor® RB 8067 CPVC, Pipe Grade
- Addcomp ADD-VANCE® CL 510 Clarification Masterbatch with Random Copolymer PP carrier
- Arlon CP-390C Bulk Compound
Copyright © lookpolymers.com All Rights Reserved