Polykemi AB SCANAMID 66 A33^E F45 Nylon 66, Glass Fiber Reinforced, Elastomer Modified

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 40% Glass Fiber Filled , Nylon 66, 50% Glass Fiber Filled
Manufacturer Polykemi AB
Trade Name SCANAMID 66
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polykemi AB SCANAMID 66 A33^E F45 Nylon 66, Glass Fiber Reinforced, Elastomer Modified.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by Polykemi AB
Physical Properties Metric English Comments
Density 1.48 g/cc
0.0535 lb/in³
ISO 1183
Filler Content 45 %
45 %
±2%; Polykemi
Linear Mold Shrinkage 0.0030 cm/cm
0.0030 in/in
With Flow; ISO 2577
0.0080 cm/cm
0.0080 in/in
Across Flow; ISO 2577
Mechanical Properties Metric English Comments
Tensile Strength at Break <= 150 MPa
<= 21800 psi
ISO/R527
Elongation at Break 4.5 %
4.5 %
ISO/R527
Elongation at Yield 3.7 %
3.7 %
ISO/R527
Flexural Strength <= 250 MPa
<= 36300 psi
ISO 178
Flexural Modulus 11.0 GPa

@Temperature 23.0 °C
 1600 ksi

@Temperature 73.4 °F
 ISO 178
Charpy Impact Unnotched NB

@Temperature 23.0 °C
 NB

@Temperature 73.4 °F
 ISO 179
NB

@Temperature -20.0 °C
 NB

@Temperature -4.00 °F
 ISO 179
Charpy Impact, Notched 1.40 J/cm²

@Temperature -20.0 °C
 6.66 ft-lb/in²

@Temperature -4.00 °F
 ISO 179
2.00 J/cm²

@Temperature 23.0 °C
 9.52 ft-lb/in²

@Temperature 73.4 °F
 ISO 179
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 230 °C
446 °F
120°C/h; ISO 75/1
Vicat Softening Point 240 °C

@Load 5.001 kg
 464 °F

@Load 11.03 lb
 50°C/h; ISO 306