Cosmic Plastics D72 Short Glass Fiber Filled Ortho Diallyl Phthalate Molding Compound
| Category | Polymer , Thermoset , Diallyl Phthalate (DAP) , Diallyl Phthalate (DAP) Molding Compound, Short Glass Fiber Filled , Filled/Reinforced Thermoset |
| Manufacturer | Cosmic Plastics |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Cosmic Plastics D72 Short Glass Fiber Filled Ortho Diallyl Phthalate Molding Compound.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by the manufacturer.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.82 g/cc | 0.0658 lb/in³ | |
| Apparent Bulk Density | 0.730 g/cc | 0.0264 lb/in³ | |
| Water Absorption | 0.25 % | 0.25 % | 48 hrs, 50°C |
| Linear Mold Shrinkage | 0.0010 - 0.0040 cm/cm | 0.0010 - 0.0040 in/in | typical. |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 41.0 - 69.0 MPa | 5950 - 10000 psi | |
| Flexural Strength | 97.0 MPa | 14100 psi | |
| Compressive Strength | 172 MPa | 24900 psi | |
| Izod Impact, Notched | 0.450 J/cm | 0.843 ft-lb/in |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 16.0 µm/m-°C @Temperature 20.0 °C |
8.89 µin/in-°F @Temperature 68.0 °F |
|
| Deflection Temperature at 1.8 MPa (264 psi) | 260 °C | 500 °F | Heat Distortion temperature |
| Flammability, UL94 | V-0 @Thickness 1.60 mm |
V-0 @Thickness 0.0630 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | >= 1.00e+17 ohm-cm | >= 1.00e+17 ohm-cm | |
| Surface Resistance | >= 1.00e+17 ohm | >= 1.00e+17 ohm | |
| Dielectric Constant | 4.2 @Frequency 1e+6 Hz |
4.2 @Frequency 1e+6 Hz |
Wet |
| 4.3 @Frequency 1000 Hz |
4.3 @Frequency 1000 Hz |
Wet | |
| Dielectric Strength | 14.0 kV/mm | 356 kV/in | Wet, Step by Step |
| Dissipation Factor | 0.011 @Frequency 1000 Hz |
0.011 @Frequency 1000 Hz |
Wet |
| 0.015 @Frequency 1e+6 Hz |
0.015 @Frequency 1e+6 Hz |
Wet | |
| Arc Resistance | 145 sec | 145 sec |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 135 - 165 °C | 275 - 329 °F | Molding temperature |
Users viewing this material also viewed the following:
- Polymer Resources PPX-SF2 Modified PPO, Structural Foam Grade, Standard Flow (Unverified Data**)
- Sharadaa Ceramics KYANITE HT Mullite
- Sax Polymers SAXAMID 226F6T3 Nylon 6.6, 30% Glass Fiber
- Covestro Bayfill® EA 4003 Polyurethane Energy-Absorbing Semi-Rigid Foam, Rigid Grade, MDI-based 2-Component Liquid System
- Esstech X-756-0000 1,3-Glycerol Dimethacrylate/Maleate Adduct, C15H18O8
- Chem Polymer Chemlon 218 GV Nylon 6, 18% Glass Reinforced
- Wellman Wellamid® XT1863-BK1 Impact Modified Nylon 66
- Williams Advanced Alloys Wambraze™ WB1004 Solder
Copyright © lookpolymers.com All Rights Reserved