SABIC Innovative Plastics LNP THERMOCOMP OCF62 PPS - Branched
| Category | Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP OCF62 PPS - Branched.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* OCF62 is a compound based on PPS-Branched resin containing 10% Carbon Fiber, 30% Glass Fiber. Added feature of this material includes: Easy Molding
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.66 g/cc | 0.0600 lb/in³ | ASTM D792 |
| 1.66 g/cc | 0.0600 lb/in³ | ISO 1183 | |
| Linear Mold Shrinkage, Flow | 0.0010 - 0.0040 cm/cm @Time 86400 sec |
0.0010 - 0.0040 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0070 - 0.010 cm/cm @Time 86400 sec |
0.0070 - 0.010 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 133 MPa | 19300 psi | 5 mm/min; ISO 527 |
| 157 MPa | 22800 psi | Type I, 5 mm/min; ASTM D638 | |
| Tensile Strength, Yield | 133 MPa | 19300 psi | 5 mm/min; ISO 527 |
| 157 MPa | 22800 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 0.50 % | 0.50 % | 5 mm/min; ISO 527 |
| 0.70 % | 0.70 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 0.50 % | 0.50 % | 5 mm/min; ISO 527 |
| 0.70 % | 0.70 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 28.6 GPa | 4150 ksi | 1 mm/min; ISO 527 |
| 30.32 GPa | 4398 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 206 MPa | 29900 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Yield Strength | 46.0 MPa | 6670 psi | 2 mm/min; ISO 178 |
| 205 MPa | 29700 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 19.07 GPa | 2766 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| 20.56 GPa | 2982 ksi | 2 mm/min; ISO 178 | |
| Izod Impact, Notched | 0.630 J/cm | 1.18 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 2.60 J/cm | 4.87 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 6.00 kJ/m² | 2.86 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 13.0 kJ/m² | 6.19 ft-lb/in² | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 1.02 µm/m-°C @Temperature 23.0 - 60.0 °C |
0.567 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 |
| 1.02 µm/m-°C @Temperature -40.0 - 40.0 °C |
0.567 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 | |
| CTE, linear, Transverse to Flow | 4.57 µm/m-°C @Temperature -40.0 - 40.0 °C |
2.54 µin/in-°F @Temperature -40.0 - 104 °F |
ASTM E 831 |
| 4.60 µm/m-°C @Temperature 23.0 - 60.0 °C |
2.56 µin/in-°F @Temperature 73.4 - 140 °F |
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 281 °C | 538 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 280 °C @Thickness 3.20 mm |
536 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 268 °C | 514 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 267 °C @Thickness 3.20 mm |
513 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Nye Lubricants 822S-1 (FG) Synthetic Oil
- SABIC Innovative Plastics Geloy INP983 ASA
- SABIC Innovative Plastics Lexan® LS3 PC
- Lanxess Durethan® DP 1801/30 H3.0 000000 Nylon 6, 30% Milled Glass Fiber
- Lucobit Lucolast® 7010 Ethylene Butyl Acrylate Asphalt Additive
- SABIC Innovative Plastics LNP LUBRICOMP Noryl_NF1520 PPE+PS
- Tra-Con Tra-Bond 7560D Hydrolytically Stable Adhesive
- Clariant Renol PBT1700G30BK Polybutylene Terephthalate, 30% Glass Reinforced, Flame Retardant
Copyright © lookpolymers.com All Rights Reserved