SABIC Innovative Plastics NORYL FN150 PPE+HIPS (Europe-Africa-Middle East)

Category Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polystyrene (PS)
Manufacturer SABIC Innovative Plastics (GE Plastics)
Trade Name Noryl
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF SABIC Innovative Plastics NORYL FN150 PPE+HIPS (Europe-Africa-Middle East).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
NORYL FN150 twin wall foam meets UL standard 94 V-0/5V ratings at 4 mm wall thickness. These unique flammability characteristics make FN150 the supreme choice for designing optimum wall thickness in computer and business machine applications. Noryl FN150 twin wall foam maintains the advantages of the Engineering Structural Foam principle at optimal cost efficiency.
Physical Properties Metric English Comments
Specific Gravity 0.900 g/cc
0.900 g/cc
ASTM D792
Linear Mold Shrinkage, Flow 0.0060 - 0.0080 cm/cm
0.0060 - 0.0080 in/in
on Tensile Bar; SABIC Method
Melt Index of Compound 6.0 g/10 min

@Load 2.16 kg,
Temperature 280 °C
6.0 g/10 min

@Load 4.76 lb,
Temperature 536 °F
MVR [cm^3/10 min]; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 40.0 MPa
5800 psi
50 mm/min; ISO 527
Tensile Strength, Yield 45.0 MPa
6530 psi
50 mm/min; ISO 527
Elongation at Break 40 %
40 %
50 mm/min; ISO 527
Elongation at Yield 3.0 %
3.0 %
50 mm/min; ISO 527
Flexural Yield Strength 70.0 MPa
10200 psi
2 mm/min; ISO 178
Flexural Modulus 2.00 GPa
290 ksi
2 mm/min; ISO 178
Izod Impact, Notched (ISO) 15.0 kJ/m²
7.14 ft-lb/in²
80*10*4; ISO 180/1A
Gardner Impact 10.0 - 20.0 J
7.38 - 14.8 ft-lb
SABIC Method
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 75.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
41.7 µin/in-°F

@Temperature 73.4 - 176 °F
ISO 11359-2
CTE, linear, Transverse to Flow 85.0 µm/m-°C

@Temperature 23.0 - 80.0 °C
47.2 µin/in-°F

@Temperature 73.4 - 176 °F
ISO 11359-2
Thermal Conductivity 0.240 W/m-K
1.67 BTU-in/hr-ft²-°F
ISO 8302
Vicat Softening Point 105 °C
221 °F
Rate B/120; ISO 306
UL RTI, Electrical 50.0 °C
122 °F
UL 746B
UL RTI, Mechanical with Impact 50.0 °C
122 °F
UL 746B
UL RTI, Mechanical without Impact 50.0 °C
122 °F
UL 746B
Flammability, UL94 V-0

@Thickness 4.00 mm
V-0

@Thickness 0.157 in
UL 94
5VA

@Thickness 4.00 mm
5VA

@Thickness 0.157 in
UL 94
Oxygen Index 29 %
29 %
ISO 4589
Electrical Properties Metric English Comments
Dielectric Constant 2.2

@Frequency 1.00e+6 Hz
2.2

@Frequency 1.00e+6 Hz
IEC 60250
2.3

@Frequency 50.0 - 60.0 Hz
2.3

@Frequency 50.0 - 60.0 Hz
IEC 60250
Dissipation Factor 0.0039

@Frequency 1.00e+6 Hz
0.0039

@Frequency 1.00e+6 Hz
IEC 60250
0.0047

@Frequency 50.0 - 60.0 Hz
0.0047

@Frequency 50.0 - 60.0 Hz
IEC 60250
Descriptive Properties Value Comments
Weight Reduction 20%
SABIC Method