Total PPC 4720XWZ Polypropylene, Impact Copolymer

Category	Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Molded
Manufacturer	Total Atofina
Trade Name	PPC
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Total PPC 4720XWZ Polypropylene, Impact Copolymer.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

TOTAL Petrochemicals Polypropylene 4720XWZ is a nucleated impact copolymer with a Melt Flow index of 25 g/10 min.TOTAL Polypropylene 4720XWZ is characterized by improved stiffness, creep resistance, high impact resistance, antistatic properties and has been formulated to allow faster cycling through early demolding.Total Polypropylene 4720XWZ has been developed specifically for the injection molding of garden furniture, housewares and thin-walled articles.Information provided by Total Petrochemicals.

Physical Properties	Metric	English	Comments
Specific Gravity	0.905 g/cc	0.905 g/cc	ASTM D1505
Melt Flow	25 g/10 min	25 g/10 min	ASTM D1238

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	27.0 MPa	3920 psi	ASTM D638
Elongation at Yield	6.0 %	6.0 %	ASTM D638
Flexural Modulus	1.45 GPa	210 ksi	ASTM D790
Izod Impact, Notched	0.450 J/cm @Temperature -20.0 °C	0.843 ft-lb/in @Temperature -4.00 °F	ASTM D256
	1.05 J/cm @Temperature 23.0 °C	1.97 ft-lb/in @Temperature 73.4 °F	ASTM D256
Charpy Impact, Notched	0.450 J/cm² @Temperature -20.0 °C	2.14 ft-lb/in² @Temperature -4.00 °F	DIN 53453
	0.950 J/cm² @Temperature 23.0 °C	4.52 ft-lb/in² @Temperature 73.4 °F	DIN 53453

Thermal Properties	Metric	English	Comments
Melting Point	160 - 165 °C	320 - 329 °F	TOTAL Method
Deflection Temperature at 0.46 MPa (66 psi)	90.0 °C	194 °F	Pressure unspecified; ASTM D648
Vicat Softening Point	150 °C	302 °F	ASTM D1525