SABIC Innovative Plastics Lexan® OQ3420 PC (Asia Pacific)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Lexan® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Lexan® OQ3420 PC (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Medium Viscosity, UV-stabilized grade for ophthalmic lenses.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 10.5 g/10 min @Load 1.20 kg, Temperature 300 °C |
10.5 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 65.0 MPa | 9430 psi | Type I, 50 mm/min; ASTM D638 |
| Tensile Strength, Yield | 62.0 MPa | 8990 psi | Type I, 50 mm/min; ASTM D638 |
| Flexural Yield Strength | 93.0 MPa | 13500 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 2.34 GPa | 339 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 7.47 J/cm | 14.0 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 137 °C @Thickness 6.40 mm |
279 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 132 °C @Thickness 6.40 mm |
270 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| Vicat Softening Point | 152 °C | 306 °F | Rate B/50; ASTM D1525 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Refractive Index | 1.586 | 1.586 | ASTM D542 |
| Haze | 1.0 % @Thickness 2.54 mm |
1.0 % @Thickness 0.100 in |
ASTM D1003 |
| Transmission, Visible | 89 % | 89 % | 2.54 mm; ASTM D1003 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Purity, particles per gram > 50 microns | 1 | SABIC Method |
| Purity, particles per gram 20-50 microns | 40 | SABIC Method |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® LUX2110T_ PC (Europe-Africa-Middle East)
- LG Chemical LUMID GP2309A(W) PA6+GF30%, General Purpose
- LG Chemical Lupox® DP1000DU PBT
- Huntsman AVALON® 65 AK Thermoplastic Polyurethane
- Sichuan Deyang Haton® ha Polyphenylene Sulfide Coating
- Silon Taborex TA 1132 HD Chemically-Crosslinkable HDPE Compound
- Total Lumicene® mPE M 2704 EP S01 Metallocene Polyethylene, Blown Film
- DuPont Teijin Films Teijin® Tetoron® HSL Polyester Film, 700 Gauge
- A. Schulman ComAlloy Hiloy® 284 PPO Alloy, Glass/Graphite Reinforced
Copyright © lookpolymers.com All Rights Reserved