SABIC Innovative Plastics Lexan® IM1063 PC (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Lexan® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Lexan® IM1063 PC (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Lexan* IM1063 is a impact modified polycarbonate gradeThis data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.15 % | 0.15 % | 23°C / 50% RH; ISO 62 |
| Water Absorption at Saturation | 0.35 % @Temperature 23.0 °C |
0.35 % @Temperature 73.4 °F |
ISO 62 |
| Melt Flow | 6.0 g/10 min @Load 1.20 kg, Temperature 300 °C |
6.0 g/10 min @Load 2.65 lb, Temperature 572 °F |
[cm^3/10 min] Melt Volume Rate; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 65.0 MPa | 9430 psi | 50 mm/min; ISO 527 |
| Tensile Strength, Yield | 55.0 MPa | 7980 psi | 50 mm/min; ISO 527 |
| Elongation at Break | 100 % | 100 % | 50 mm/min; ISO 527 |
| Elongation at Yield | 5.0 % | 5.0 % | 50 mm/min; ISO 527 |
| Tensile Modulus | 2.20 GPa | 319 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 85.0 MPa | 12300 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 2.20 GPa | 319 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 55.0 kJ/m² @Temperature -30.0 °C |
26.2 ft-lb/in² @Temperature -22.0 °F |
80*10*3; ISO 180/1A |
| 70.0 kJ/m² @Temperature 23.0 °C |
33.3 ft-lb/in² @Temperature 73.4 °F |
80*10*3; ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
80*10*3; ISO 180/1U |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
80*10*3; ISO 180/1U | |
| Charpy Impact Unnotched | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
Edgew 80*10*3 sp=62mm; ISO 179/1eU |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
Edgew 80*10*3 sp=62mm; ISO 179/1eU | |
| Charpy Impact, Notched | 5.50 J/cm² @Temperature -30.0 °C |
26.2 ft-lb/in² @Temperature -22.0 °F |
V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA |
| 7.00 J/cm² @Temperature 23.0 °C |
33.3 ft-lb/in² @Temperature 73.4 °F |
V-notch Edgew 80*10*3 sp=62mm; ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 70.0 µm/m-°C @Temperature 23.0 - 80.0 °C |
38.9 µin/in-°F @Temperature 73.4 - 176 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 70.0 µm/m-°C @Temperature 23.0 - 80.0 °C |
38.9 µin/in-°F @Temperature 73.4 - 176 °F |
ISO 11359-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 122 °C | 252 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| Vicat Softening Point | 140 °C | 284 °F | Rate B/50; ISO 306 |
| 143 °C | 289 °F | Rate B/120; ISO 306 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Ball Pressure Test, 125°C +/- 2°C | passes | IEC 60695-10-2 |
Users viewing this material also viewed the following:
- Polymer Resources PC-FR3A-D-[color]-3 Polycarbonate, Flame Retardant, High Flow, UV-stabilized
- Techmer ES Electrablend® PC SS10 10% Stainless Steel Filled
- SABIC Innovative Plastics Valox® ENH4550 PBT (Europe-Africa-Middle East)
- Borealis Bormed™ RF830MO Polypropylene Copolymer for Healthcare Applications
- ExxonMobil Varsol™ 140 Naphtha Non-dearomatized Fluid
- CP-Polymer-Technik Wellamid® 6000 GS 50 HWUVCP 50% Glass Sphere Filled Nylon 6, UV Stabilized Heat Stabilized, Conditioned
- 3M AC-236 Class B-1/2 Aerospace Sealant
- BASF Ultramid® B33 LV PA6
- 3A Composites Core Materials AIREX® T92.80 Easy Processing Structural Foam
Copyright © lookpolymers.com All Rights Reserved