SABIC Innovative Plastics Lexan® HF1130 PC (Asia Pacific)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Lexan® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Lexan® HF1130 PC (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
UV-stabilized. Good clarity, heat resistance, property retention and dimensional stability.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 25 g/10 min @Load 1.20 kg, Temperature 300 °C |
25 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 65.0 MPa | 9430 psi | Type I, 50 mm/min; ASTM D638 |
| Tensile Strength, Yield | 62.0 MPa | 8990 psi | Type I, 50 mm/min; ASTM D638 |
| Elongation at Break | 110 % | 110 % | Type I, 50 mm/min; ASTM D638 |
| Flexural Yield Strength | 93.0 MPa | 13500 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 2.30 GPa | 334 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 6.40 J/cm | 12.0 ft-lb/in | ASTM D256 |
| Tensile Impact Strength | 378 kJ/m² | 180 ft-lb/in² | Type S; ASTM D1822 |
| Dart Drop, Total Energy | 54.0 J | 39.8 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 126 °C @Thickness 6.40 mm |
259 °F @Thickness 0.252 in |
unannealed; ASTM D648 |
| UL RTI, Electrical | 100 °C | 212 °F | UL 746B |
| UL RTI, Mechanical with Impact | 100 °C | 212 °F | UL 746B |
| UL RTI, Mechanical without Impact | 100 °C | 212 °F | UL 746B |
| Flammability, UL94 | V-2 @Thickness 1.47 mm |
V-2 @Thickness 0.0579 in |
UL 94 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 1.0 % @Thickness 2.54 mm |
1.0 % @Thickness 0.100 in |
ASTM D1003 |
| Transmission, Visible | 88 % | 88 % | 2.54 mm; ASTM D1003 |
Users viewing this material also viewed the following:
- Radici Radilon® A RCV3015 RKC Nylon 66-GF30
- PolyOne Bergadur™ PB40 G15 UF UV Polybutylene Terephthalate (PBT)
- DuPont™ Dartek® F-101 Nylon 6,6 Forming Film, 25 µm Thickness (discontinued **)
- Fine Organics FINALUX G1 Lubricant Additive
- Kinlead LSS11 Low Temperature Grade Heat Sealable Film (thickness: 20 µm)
- ExxonMobil PP3155 Homopolymer Grade for Nonwoven and Fiber Applications
- Arlon 51073R031 0.0311" (0.79 mm) Cured Silicone Rubber with Fiberglass Substrate
- SABIC Innovative Plastics NORYL FR9310 PPE (Europe-Africa-Middle East)
- Bhansali Engineering Abstron MIF45EP ABS Injection Molding Grade
Copyright © lookpolymers.com All Rights Reserved